Abstract:In this work, a simple in-situ water-bath method is used to load Cu2O hollow nanospheres (named as H-Cu2O) on TiO2 nanosheets (named as TiO2-NS). H-Cu2O of 160–250 nm in diameter is uniformly supported on the surface of TiO2-NS. H-Cu2O has a novel hollow core-shell structure with a double shell. Specifically, the diameters of inner hollow spheres are 80–90 nm and the thickness of the outer shell and inner shell are about 40 nm and 25 nm, respectively. It is conjectured that the outer and inner shells of H-Cu2O can both provide adsorption and reaction sites, favoring the photocatalytic reaction. The UV–visible diffused reflectance spectra show that compared with TiO2-NS, the H-Cu2O/TiO2-2 sample with adding 80 mg of TiO2-NS shows a stronger visible light absorption. Furthermore, the steady-state photoluminescence (PL) and photocurrent spectra show that H-Cu2O/TiO2-2 has a weaker PL intensity at about 370 nm and 6 times higher photocurrent intensity than TiO2-NS, demonstrating that H-Cu2O/TiO2-2 has higher charge separation efficiency. Compared with TiO2-NS, the photocatalytic activity of H-Cu2O/TiO2-2 under UV light (λ ≤ 400 nm) increase by 6.3 times for the degradation of methyl orange. The improved photocatalytic activity can be attributed to the enlarged BET areas (6.1 m2 g-1/H-Cu2O/TiO2-2 vs. 3.8 m2 g-1/TiO2-NS), the enhanced light adsorption, and the improved charge separation efficiency. The reported in-situ water-bath method is simple, mild, and general, which could be extended to other novel composite materials.

Homogeneous Synthesis of SiO2@TiO2 Nanocomposites with Controllable Shell Thickness and Their Enhanced Photocatalytic Activity.

Nanoporous core–shell Cu@Cu2O nanocomposites with superior photocatalytic properties towards the degradation of methyl orange

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

Synthesis of Small Yolk–shell Fe3O4@TiO2 Nanoparticles with Controllable Thickness As Recyclable Photocatalysts

Novel TiO₂-Pt@SiO₂ nanocomposites with high photocatalytic activity

Novel Tio2-Pt@Sio2 Nanocomposites With High Photocatalytic Activity

Fabrication of hydroxyl group modified monodispersed hybrid silica particles and the h-SiO2/TiO2 core/shell microspheres as high performance photocatalyst for dye degradation

Preparation of Porous SiO<SUB>2</SUB>-TiO<SUB>2</SUB> Nanocomposites and Their Photocatalytic Activity: Preparation of Porous SiO<SUB>2</SUB>-TiO<SUB>2</SUB> Nanocomposites and Their Photocatalytic Activity

Hydrolytic Modification of SiO2 Microspheres with Na2SiO3 and the Performance of Supported Nano-TiO2 Composite Photocatalyst

Preparation and Characterization of SiO<SUB>2</SUB>/TiO<SUB>2</SUB>-Pt Core/Shell Nanostructures and Evaluation of Their Photocatalytic Activity

Yolk-Shell Tio2-Nrs@Sio2 with Enhanced Photocatalytic Hydrogen Production

Preparation of Porous SiO_2-TiO_2 Nanocomposites and Their Photocatalytic Activity

Synthesis of mesoporous SiO2@TiO2 core/shell nanospheres with enhanced photocatalytic properties

Preparation of In2O3@TiO2 core-shell spherical nanocomposites with the enhanced photocatalytic activity under solar light irradiation

Synthesis of Highly Monodispersed CdS/SiO<SUB>2</SUB> Core Shell Nanoparticles and Their Photocatalytic Activities

Facile Synthesis of SiO 2 @tio 2 Hybrid NPs with Improved Photocatalytic Performance

Facile Fabrication of Mesoporous SiO2@(cTiO2/BiOI) Heterojunctions with Enhanced Photocatalytic Properties Due to Large Surface Area for Contact with Pollutants

Synthesis of Highly Monodispersed Teardrop-Shaped Core–shell SiO2/TiO2 Nanoparticles and Their Photocatalytic Activities

Facile flame thermal synthesis of SiOx-C/ TiO2 microspheres with enhanced photocatalytic performance

Synthesis and photocatalytic activity of Cu2O hollow nanospheres/TiO2 nanosheets by an in-situ water-bath method

Facile Synthesis of CdS@TiO2 Core–shell Nanorods with Controllable Shell Thickness and Enhanced Photocatalytic Activity under Visible Light Irradiation