Abstract:The axial compressive strength of carbon fiber reinforced polymer composites (CFRP) is significantly lower than the tensile strength, which hinders its wide applications. The failure mechanism of CFRP under unidirectional compression parallel to the fiber alignment direction is complex, but research on this issue is limited. In order to understand this mechanism more deeply and intuitively, a two-dimensional microscopic numerical model is proposed. The influences of various properties of the fiber and matrix on the compressive strength of CFRP are investigated, including the axial elastic modulus of the fiber (E f1), the transverse elastic modulus of the fiber (E f2), the shear modulus of the fiber (G f12), the elastic modulus of the matrix (E m), the proportional strength limit of the matrix (σ p), the yield strength of the matrix (σ s) and the degree of initial fiber misalignment. Results show that the model is capable of explaining the failure mechanism of CFRP under a unidirectional compressive load. Shear stress plays an important role in the compressive failure process. The localization of shear stress caused by initial fiber misalignment leads to plastic yield of the matrix and finally a kink band. Changes in these propertiesdirectly affect the concentration of shear stress in the defect areas, thereby affecting the compressive strength of the CFRP. When the values of E f1, E f2, G f12, E m, σ p, σ s are separately increased by 10% or the degree of initial fiber misalignment is decreased by 10%, the compressive strength of CFRP is increased by 2.33%, 0%, 0.39%, 3.38%, 1.17%, 2.30% and 2.52% respectively. E m has the greatest influence on the compressive strength of CFRP, followed by the initial fibermisalignment. The effects of the plastic properties of the matrix on the compressive strength of CFRP are obvious.

Effects of Inter-Fiber Spacing and Thermal Residual Stress on Transverse Failure of Fiber-Reinforced Polymer–matrix Composites

Micro Failure Analysis of Fiber Metal Laminates

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

Multi-Scale Modeling and Damage Analysis of Composite with Thermal Residual Stress

Initial Damage Induced by Thermal Residual Stress and Microscopic Failure Analysis of Carbon-Fiber Reinforced Composite under Shear Loading

A Microscale Analysis of Thermal Residual Stresses in Composites with Different Ply Orientations

Micromechanical analysis of stochastic fiber/matrix interface strength effect on transverse tensile property of fiber reinforced composites

Out-of-plane Tensile Failure Behavior of Fiber Reinforced Composites Due to Lay-Up Temperature Induced Intra-Ply and Inter-Ply Voids

Investigation on the Effects of Microstructure on Machining Unidirectional Carbon Fiber Reinforced Polymer Composites with a Modified Force Model

Theoretical and Experimental Studies on Residual Stresses of Advanced Polymer Composites

Computational modeling of micro curing residual stress evolution and out-of-plane tensile damage behavior in fiber-reinforced composites

Effects of fiber and matrix properties on the compression strength of carbon fiber reinforced polymer composites

Effects of interfacial residual stress on mechanical behavior of SiCf/SiC composites

Residual stress variation in SiCf/SiC composite during heat treatment and its effects on mechanical behavior

Microscale viscoplastic analysis of unidirectional CFRP composites under the influence of curing process

Effect of resin-rich areas on failure behavior of unidirectional CFRP under transverse pure shear

Effect of resin-rich zones on the failure response of carbon fiber reinforced polymers

Study of the effect of void defects on the mechanical properties of fiber reinforced composites

The effect of imperfect bonding on stress distribution in fibrous composites

Effect of fiber roughness on interfacial friction of fiber reinforced ceramic matrix composites

Microscopic Progressive Damage Simulation of Unidirectional Composite Based on the Elastic–plastic Theory