Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Multi-Scale Modeling and Damage Analysis of Composite with Thermal Residual Stress

Progressive failure analysis of 2D woven composites at the meso-micro scale

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Initial Damage Induced by Thermal Residual Stress and Microscopic Failure Analysis of Carbon-Fiber Reinforced Composite under Shear Loading

Damage Evolution and Multi-Scale Analysis of Carbon Fiber-Reinforced Cross-Ply Laminate with Thermal Residual Stress

A Multi-Scale Modeling Scheme for Damage Analysis of Composite Structures Based on the High-Fidelity Generalized Method of Cells

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

Microscopic Progressive Damage Simulation of Unidirectional Composite Based on the Elastic–plastic Theory

A Dynamic Monte Carlo Microscopic Damage Model Incorporating Thermo-Mechanical Coupling in a Unidirectional Composite

Finite Element Analysis of Thermal Residual Stress in Unidirectional Fiber Reinforced Composite

Micromechanical Modeling of Viscoplastic Behavior of Laminated Polymer Composites with Thermal Residual Stress Effect

Multiscale Progressive Damage Model for Plain Woven Composites

An Innovative Micromechanics-Based Multiscale Damage Model of 3D Woven Composites Incorporating Probabilistic Fiber Strength Distribution

Hierarchical Multi-Scale Analysis of the Effect of Varying Fiber Bundle Geometric Properties on the Mechanical Properties of 3D Braided Composites

Different Effects of Interfacial Properties on the Tensile and Compressive Damage Mechanisms of 3D Woven Composites: Multiscale Damage Model and Numerical Comparative Study

Multi-scale Progressive Failure Simulation of 3D Woven Composites under Uniaxial Tension

3D Orthogonal Woven Carbon/Carbon Composites: Micromechanical Modeling and Damage Analysis

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Investigation on the off-axis tensile failure behaviors of 3D woven composites through a coupled numerical-experimental approach

A Note On The Monte-Carlo Simulation Of The Tensile Deformation And Failure Process Of Unidirectional Composites

A Multi-Scale Stochastic Fracture Model for Characterizing the Tensile Behavior of 2D Woven Composites