Corrosion Inhibition Mechanism of Microarc Oxidized AZ31 Magnesium Alloy in Simulated Body Fluid

顾艳红,宁成云,赵杰,刘淑晶,窦艳涛,熊文名

2013-01-01

Abstract:The effect of immersion time on corrosion behavior of microarc-oxidized AZ31 Mg alloy in a simulated body fluid was studied. The microarc oxidation was performed in an electrolyte of 30 g/L sodium phosphate (Na3PO4) at a voltage of 250 V and a pulse frequence of 3000 Hz for, 5 min. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) were used to characterize the corrosion behavior. The corrosion current density increases during the first 14 days and then decreases in the subsequent days. The electrochemical impedance is in accord with the result of the corrosion current density. The characterization of corrosion products revealed that hydroxyapatite (HA) was formed on the surface of the samples. The ratio Ca/P of the corrosion products was determined by the X-ray fluorescence (XRF) technique, and the value is around 1.67. The corrosion resistance of the microarc oxidized samples is enhanced due to the formation of a corrosion product after immersion in simulated body fluid for more than 14 days. The corrosion inhibition mechanism of the corrosion process is discussed and presented with a physical model.