Abstract:This work attempts to prepare ethylene-a-olefin copolymer with relatively narrow composition distribution by modification of TiCl4/MgCl2 type supported Ziegler-Natta catalyst. A TiCl4/ID/MgCl2 type catalyst, where ID is a diester, was treated at room temperature with 2,6-'Pr2C6H3-OH at phenol: Ti molar ratio of 1:1 and the modified catalyst was analyzed for contents of titanium and aryloxy group. It was found that about one third of the titanium atoms in the modified catalyst (M-cat) was connected with an aryloxy group, but its Ti content was decreased to 1.44 wt% from 2.36 wt% of the original catalyst (O-cat). Ethylene-1-hexene copolymerization was conducted in n-heptane with M-cat or O-cat as catalyst and triisobutyl aluminium or methylaluminoxane as cocatalyst. The M-cat showed similar activity as the O-cat in catalyzing the copolymerization, but presented a weaker comonomer activation effect than the latter. The 1-hexene content of copolymer synthesized by M-cat was lower than that of the product of O-cat at the same conditions, but had a markedly narrower composition distribution. Each copolymer sample was fractionated into two fractions by extraction with boiling n-heptane, and the soluble part contains much more 1-hexene units than the insoluble part. The ratio of I-hexene content in the soluble fraction to that of the insoluble fraction was higher than 18 in copolymer prepared with O-cat, but this ratio was reduced to 3.7 when M-cat was used as the catalyst. On the other hand, the soluble part of copolymer prepared with M-cat showed a more random sequence distribution than that of the O-cat. The distributions of active centers in both the M-cat and O-cat were studied by deconvolution of the polymer's molecular weight distribution curves with multiple Flory most-probable distribution function. Both catalysts showed a broad molecular weight distribution that can be ascribed to 5 similar to 6 types of active centers, but the introduction of aryloxy group in the catalyst caused marked changes in the active center distribution. Possible mechanism of the catalyst modification was proposed.

Ethylene/1-Hexene copolymerization with a novel SiO2-supported inorganic and organic hybrid chromium-based catalyst

A MOF-supported Chromium Catalyst for Ethylene Polymerization Through Post-Synthetic Modification

A novel SiO2-supported inorganic and organic hybrid chromium-based catalyst for ethylene polymerization

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Effect of Catalysts Supporting on Tandem Polymerization of Ethylene Stock in Synthesis of Ethylene-1-Hexene Copolymer

ETHYLENE POLYMERIZATION WITH CORE-SHELL ZIEGLER-NATTA HYBRID CATALYSTS

Synthesis of Ethylene‐1‐hexene Copolymers from Ethylene Stock by Tandem Action of Bis(2‐dodecylsulfanyl‐ethyl) Amine‐crcl3 and Et(Ind)2ZrCl2

High Temperature High Pressure Tandem Polymerization of Ethylene for Synthesis of Ethylene‐1‐Hexene Copolymers from Single Reactor with SNS‐Cr and CGC‐Ti Catalysts

Tandem Action of Sns-Cr and Cgc-Ti in Preparation of Ethylene-1-Hexene Copolymers from Ethylene Feedstock

Tuning the Short Chain Branch Distribution of Ethylene and 1-Hexene Copolymers by SiO2-supported Silyl Chromate Catalyst with Different Al-alkyl Co-Catalysts

Novel SiO2‐Supported Silyl‐Chromate(Cr)/Imido‐Vanadium(V) Bimetallic Catalysts Producing Polyethylene and Ethylene/1‐Hexene Copolymers with Bimodal Molecular‐Weight Distribution

Introduction of chromium species into the (SiO 2 /MgO/MgCl 2 )·TiCl x Ziegler–Natta catalyst for better catalytic performance

Gas Phase Ethylene Polymerization over SiO2-supported Organosilyl Chromate UCC S-2 Catalyst Using a High-Speed Stirred-Autoclave Reactor

Introduction of Titanium Species into Fluorine-Modified SiO2- Supported Cr-V Bimetallic Catalyst for Ethylene Polymerization and Ethylene/1-Hexene Copolymerization

Novel layered calcosilicate-immobilized iron-based diimine catalyst for ethylene polymerization

Ethylene Polymerization by New Chromium Catalysts Based on Carborane [sso] Ligands

Effect of Mo-Modification over Phillips Crox/Sio2 Catalyst for Ethylene Polymerization

Switching from Ethylene Polymerization to Nonselective Oligomerization over a Homogeneous Model Catalyst: A Triphenylsiloxy Complex of Chromium(vi)

Recent Progress on Molecular Modeling of Ethylene Polymerization/Oligomerization Catalyzed by Chromium-Based Catalysts

Ethylene-1-Hexene Copolymerization with A 2,6-Diisopropylphenol Modified Supported Ziegler-Natta Catalyst

A Novel SiO2-Supported Fluorine Modified Chromium–Vanadium Bimetallic Catalyst for Ethylene Polymerization and Ethylene/1-Hexene Copolymerization