Abstract:A series of Fe-Mn/Al2O3 catalysts were prepared and studied for low temperature selective catalytic reduction (SCR) of NO with NH3 in a fixed-bed reactor. The effects of Fe and Mn on NO conversion and the deactivation of the catalysts were studied. N2 adsorption-desorption, X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, H2 temperature-programmed reduction, NH3 temperature-programmed desorption, X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the catalysts. The 8Fe-8Mn/Al2O3 catalyst gave 99% of NO conversion at 150 °C and more than 92.6% NO conversion was obtained in a wide low temperature range of 90–210 °C. XPS analysis demonstrated that the Fe3+ was the main iron valence state on the catalyst surface and the addition of Mn increased the accumulation of Fe on the surface. The higher specific surface area, enhanced dispersion of amorphous Fe and Mn, improved reduction properties and surface acidity, lower binding energy, higher Mn4+/Mn3+ ratio and more adsorbed oxygen species resulted in higher NO conversion for the 8Fe-8Mn/Al2O3 catalyst. In addition, the SCR activity of the 8Fe-8Mn/Al2O3 catalyst was only slightly decreased in the presence of H2O and SO2, which indicated that the catalyst had better tolerance to H2O and SO2. The reaction temperature was crucial for the SO2 resistance of catalyst and the decrease of catalytic activity caused by SO2 was mainly due to the sulfate salts formed on the catalyst.

H2O and SO2 Deactivation Mechanism of MnOx/MWCNTs for Low-Temperature SCR of NOx with NH3

Sulfur/water resistance and regeneration of MnO -CeO2/TiO2 catalyst for low-temperature selective catalytic reduction of NO

The Influence of the Pore Structure on the SO2 Tolerance for Selective Catalytic Reduction of NOx with NH3 over MnOx-TiO2/MWCNTs Catalysts

Sulfur and Water Resistance of Mn-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOx: A Review

SO 2 and H 2 O Poisoning Resistance of Manganese Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO X

Effect of SO2 on Activated Carbon Honeycomb Supported CeO2–MnOx Catalyst for NO Removal at Low Temperature

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Low-temperature SCR of NOx by NH3 over MnOx/SAPO-34 prepared by two different methods: a comparative study

NH3-SCR Performance of Mn-Fe/TiO2 Catalysts at Low Temperature in the Absence and Presence of Water Vapor

NH 3 -SCR Performance of Mn-Fe/TiO 2 Catalysts at Low Temperature in the Absence and Presence of Water Vapor

Mechanism of SO2 Influence on Mn/TiO2 for Low Temperature SCR Reaction

Effect of Water Vapor on NH3–NO/NO2 SCR Performance of Fresh and Aged MnOx–NbOx–CeO2 Catalysts

Highly efficient NH3-SCR of NO over MnFeW/Ti catalyst at low temperature: SO2 tolerance and reaction mechanism

Prominent difference in the deactivation rate and mechanism of V2O5/TiO2 under H2S or SO2 during selective catalytic reduction of NOx with NH3

The Mechanism of the Deactivation of MnOx/TiO2 Catalyst for Low-Temperature SCR of NO

Mechanistic Investigation of the Enhanced SO2 Resistance of Co-modified MnOx Catalyst for the Selective Catalytic Reduction of NOx by NH3

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

The Deactivation Mechanism of Toluene on MnOx-CeO2 SCR Catalyst

Facile H<sub>2</sub>O-Contributed O<sub>2</sub> Activation Strategy over Mn-Based SCR Catalysts to Counteract SO<sub>2</sub> Poisoning

Dual Effect of Sulfation on the Selective Catalytic Reduction of NO with NH3 over MnOx/TiO2: Key Factor of NH3 Distribution

SO2-promoted reduction of NO with NH3 over vanadium molecularly anchored on the surface of carbon nanotubes