Abstract:The Laves phase alloy Tb-Dy-Fe, commercially known as Terfenol-D, exhibits the giant room-temperature magnetostriction at moderate field strength of a few kOe due to its combination of high magnetostriction and low magnetocrystalline anisotropic energy. Thus, this pseudobinary rare earth iron compound has found quite a number of applications such as in magnetomechanical transducers, actuators and adaptive vibration control systems. The simultaneous measurements of magnetostriction and magnetization at various fixed compressive pre-stresses applied in the axial direction for Tb 0.3 Dy 0.7 Fe 1.95 samples are presented. The results show that the magnetostriction increases with increasing compressive stress until it reaches 1742 × 10 6 under 25 MPa, so does the coercive magnetic field. And the hysteresis loop area for magnetization and magnetostriction also increases with the increment of applied compressive stresses. But the maximum magnetic susceptibility χ (d M/ d H ) is obtained under zero stress field and the strain derivative d λ /d H increases to the highest amplitude of 0.039 × 10 −6 A −1 m at a stress level of 5 MPa. In the strain versus magnetization intensity curve, the initial flat stage mainly consisting of a 180° domain wall motion becomes shorter with increasing stress. It means more initial domains are driven to the transversal direction under the compressive stress before magnetization, which is consistent with the improvement of the magnetostriction.

Magnetostriction Of Tbfe2-Based Alloy Treated In A Semi-Solid State With A High Magnetic Field

Magnetostriction of a (110) oriented Tb0.3Dy0.7Fe1.95 polycrystals annealed under a noncoaxial magnetic field

Anisotropic magnetostriction for Tb0.3Dy0.7Fe1.95 alloys under magnetomechanical loading

Magnetoelasticity of Tb0.3dy0.7fe1.95 Alloys in A Multiaxial Stress-Magnetic Field Space

Effect of Magnetic Annealing on Magnetostrictive Performance of a 〈110〉 Oriented Crystal Tb0.3Dy0.7Fe1.95

Differential Magnetostrictive Response in Magnetically Annealed Tb0.36Dy0.64(Fe0.85Co0.15)2 with ⟨110⟩ Crystal Orientation

The Effect Of Heat-Treatment On Magnetostriction In < 110 > Oriented Crystals Tb0.36dy0.64(Fe0.85co0.15)(2)

Effect of magnetic annealing on magnetostrictive performance of a 〈1 1 0〉 oriented crystal Tb0.3Dy0.7Fe1.95

Anisotropic Magnetostriction in a ⟨110⟩ Oriented Crystal Tb0.36Dy0.64(Fe0.85Co0.15)2 after Coaxial Field Annealing

Structural Origin For The Local Strong Anisotropy In Melt-Spun Fe-Ga-Tb: Tetragonal Nanoparticles

Magnetomechanical Behaviors of Giant Magneto Strictive Materials

The Magnetostriction Of Tb(Fe0.9mnxal0.1-X)(2) Alloys

Magnetostrictive Properties of Tbdyfe Alloys along the Direction Perpendicular to the Magnetic Field

Enhanced Magnetostriction of a Narrow Hysteresis Tb0.26Dy0.54Ho0.20Fe2 Alloy

Experimental Study of the Multiaxial Ferroelastic Behavior of Tb0.3Dy0.7Fe1.95alloys

Experimental study of the multiaxial ferroelastic behavior of Tb<sub>0.3</sub>Dy<sub>0.7</sub>Fe<sub>1.95</sub>alloys

-orientation growth of Tb-Dy-Fe alloys induced by high magnetic fields during directional solidification

Magnetostriction of AlFe2B2 in High Magnetic Fields

Stress Influences on Magnetization and Magnetostriction in Magnetically Annealed Tb0.36Dy0.64(Fe0.85Co0.15)2 Polycrystals

Preparation of Terfenol-D Spherical Single-Crystal Particles and Study of Magnetostrictive Properties of Its Composites at Low Fields

MICROSTRUCTURE AND PROPERTIES OF THE HEAT TREATED DS Tb-Dy-Fe ALLOY