Magnetic Anisotropy Controlled by Distinct Interfacial Lattice Distortions at the La₁–ₓSrₓCoO₃/La₂/₃Sr₁/₃MnO₃ Interfaces
Jine Zhang,Xiaobing Chen,Qinghua Zhang,Furong Han,Jing Zhang,Hui Zhang,Hongrui Zhang,Hailin Huang,Shaojin Qi,Xi Yan,Lin Gu,Yuansha Chen,Fengxia Hu,Shishen Yan,Banggui Liu,Baogen Shen,Jirong Sun
IF: 9.5
2018-01-01
ACS Applied Materials & Interfaces
Abstract:Interface engineering is an important approach leading to multifunctional artificial materials. Although most of the previous works focused on the effects of the rotation/tilting of interfacial oxygen octahedron on perovskite multilayers, here, we report on a new kind of lattice distortion characterized by an off-center shift of the Mn ions within the MnO₆ oxygen octahedra at the interfaces of La₁–ₓSrₓCoO₃/La₂/₃Sr₁/₃MnO₃/La₁–ₓSrₓCoO₃/LaAlO₃ trilayers (x= 0–1/3), which drives the initially perpendicularly aligned magnetic axis of the La₂/₃Sr₁/₃MnO₃ (LSMO) film toward the in-plane direction, though the film is in a strongly compressive state. It is further found that the magnetic anisotropy considerably depends on the content of Sr in La₁–ₓSrₓCoO₃, enhancing as x decreases. The maximal anisotropy constant at 10 K is+ 2.5× 10⁶ erg/cm³ for the trilayers with x= 0, whereas it is− 1.5× 10⁵ erg/cm³ for a bare LSMO film on LaAlO₃. On the basis of the analysis of X-ray absorption spectroscopy and the results of density functional theory calculations, we found that the off-center displacement of the Mn ions has caused a strong orbital reconstruction at interfaces, resulting in the anomalous spin orientation against magnetoelastic coupling.