Abstract:Laser-induced damage of fused silica optics at 351 nm is a key factor limiting the output energy of high-power laser facility, especially the damage growth process. A comprehensive understanding of its damage growth behavior is of critical importance for high-power laser facility. Thus we study the laser-induced damage growth on the exit surface of fused silica under the subsequent illumination of 5 ns square pulses at 351 nm on a large-aperture high-power laser facility. Experiment is conducted with a 36 cm thick UV grade fused silica focus lens in clean atmosphere and at room temperature. 56 laser shots of 3 fluence in a range from 0.1 J/cm2 to 8.1 J/cm2 are fired during the experiment. And the damage initiation process and growth process are monitored and recorded with an online optics damage inspection instrument which has an optical resolution of about 50 m. Experimental results demonstrate that the sizes of exit-surface damage sites exponentially or linearly grow with laser shots and the damage growth rate increases with laser fluence. However, it is found that even under the same laser conditions the damage grow rate is not a fixed value, which means that besides the laser fluence other parameters also influence the damage grow process. In order to highlight some tendencies, we consider the single-shot damage growth rate and calculate the average of inside fluence bins. Statistical analysis shows that smaller sites tend to grow with larger growth rates than larger sites under the irradiation of the same laser fluence. This result indicates that damage growth rate is influenced by both laser fluence and damage site size. It suggests that the damage growth rule needs to be incorporated into a size-dependent growth effect. The result that higher growth rates are obtained for small damage sites may be related to the damage growth mechanism of fused silica. Damage crater of fused silica consists of a central core and numerous surrounding cracks. The defects in the central core absorb laser energy and yield plasma, then the plasma pressure will open the cracks on the periphery of the crater and lead to lateral and axial expansion of cracks which can be identified as damage growth. The fact that smaller sites grow faster than larger sites implies that smaller sites more efficiently couple laser energy into fracture energy. Our results have important implications for both the prediction of fused silica optics lifetime and the fundamental understanding of laser damage mechanism.

Rear-surface Light Intensification Caused by a Hertzian-conical Crack in 355-Nm Silica Optics

Analysis of Laser Intensification by Nodular Defects in Mid-Infrared High Reflectance Coatings

Numerical Simulation of the Interaction of Laser-Generated Rayleigh Waves with Subsurface Cracks

Distribution of Electric Field and Energy Flux Around the Cracks on the Surfaces of Nd-doped Phosphate Glasses.

Study on the Interaction Mechanism of Laser-Generated Rayleigh Waves and Subsurface Inclined Cracks

Behavior of 355 nm laser-induced damage growth in fused silica

Domain switching emission from the mixed-mode crack in ferroelectrics by birefringence measurement and phase field modeling

An Investigation into the Densification-Affected Deformation and Fracture in Fused Silica under Contact Sliding

Characterization of artificial indentation defects in fused silica surface and its damage performance under 355 nm nanosecond laser

A crack with surface effects in a piezoelectric material

An I-integral Method for Crack-Tip Intensity Factor Variation Due to Domain Switching in Ferroelectric Single-Crystals

Evaluation of crack initiation load of silica glass surfaces formed during subcritical crack growth

An analytical method for assessing the initiation and interaction of cracks in fused silica subjected to contact sliding

Near-Infrared Femtosecond Laser Induced Defect Formation in High Purity Silica below the Optical Breakdown Threshold

Laser-induced Damage Growth of Fused Silica at 351 Nm on a Large-Aperture High-Power Laser Facility

Enhancement of the Load Capacity of High-Energy Laser Monocrystalline Silicon Reflector Based on the Selection of Surface Lattice Defects

Laser cutting sandwich structure glass–silicon–glass wafer with laser induced thermal–crack propagation

Evolution of point defects in mechanical cracks of fused silica after CO_2 laser melting

Quantitative Estimation of Crack on or Near Surface Using Laser-Ultrasonic Surface Wave: Numerical Simulation

Microcracks in CVD diamond produced by scaife polishing