Abstract:Considerable quantities of Nd-Fe-B magnet wastes are produced every year worldwide. Some Nd-Fe-B magnet wastes in the bulk form, produced during manufacturing, have low coercivity and cannot meet the requirements for applications. Finding an effective way to reuse those wastes by improving the coercivity, without powdering or reproducing process, becomes very important for saving energy and raw materials in manufacture. In this work, the grain boundary diffusion process is carried out on waste Nd-Fe-B sintered magnets by using Pr70Cu30 as a diffusion medium. The effects of diffusion temperature, diffusion time, and annealing time on the magnetic properties of the magnets are investigated. It is found that the coercivity increases when the diffusion temperature increases from 500 to 800 degrees C, the diffusion time increases from 1 to 3 h, or the annealing time increases from 1 to 3 h. By comparing the diffused sample with the simply heat treated sample, we find that the coercivity enhancement by grain boundary diffusion process indeed results from the infiltration of Pr and Cu elements. The coercivity of the magnet increases by 51.9%, from 7.88 kOe (1 Oe = 79.5775 A/m) to 11.97 kOe, after 4-hour diffusion at 800 degrees C followed by 3-hour annealing, with a negligible reduction of remanence B-r, achieving a 99.8% recovery of coercivity compared with the commercial N35 magnet. It is noted that 500 degrees C annealing for 3 h after 800 degrees C diffusion only slightly increases the coercivity by 4.6%, from 11.44 kOe to 11.97 kOe, which indicates that the annealing process after Pr-Cu grain boundary diffusion may be not indispensable. Based on the microstructure analysis, the diffusion of Pr and Cu is confirmed. However, the distributions of Pr and Cu are inhomogeneous within a range of tens of microns near the surface even though the diffusion has spread throughout the magnet. The structure of main phase grains separated by the continuous grain boundary phase is formed after the grain boundary diffusion process while the core-shell structure is not observed, which suggests that the modification of the grain boundary structure is the main reason for the coercivity improvement. Cu element plays an important role in forming continuous grain boundary phase. In addition, the electrochemical corrosion test shows that higher corrosion current is obtained in the diffused magnet than in the original magnet, though the corrosion potential is improved. The reduced corrosion resistance may be related to the increased RE-rich phase content and the formation of continuous grain boundary phase. The present work is of great importance for increasing the production yield of Nd-Fe-B magnets.

Improvement of Coercivity and Thermal Stability of Anisotropic Nd13fe79.4b7nb0.3ga0.3 Powders by Diffusion of Pr-Cu Alloys

Coercivity Enhancement in Anisotropic Pr13fe79.4b7nb0.3ga0.3 Powders

Coercivity enhancement in HDDR near-stoichiometric ternary Nd-Fe-B powders

Coercivity Enhancement by Grain Refinement for Anisotropic Nd 2 Fe 14 B-type Magnetic Powders

Coercivity Enhancement Of Anisotropic Die-Upset Nd-Fe-B Powders By Pr-Cu Alloy Diffusion

Anisotropic ternary Ce13Fe80B7 powders prepared by hydrogenation-disproportionation-desorption-recombination process and the diffusion of Ce-Cu eutectic alloys

Anisotropic Ternary Pr13Fe80B7 Powders Prepared by Hydrogenation Disproportionation Desorption Recombination Process

Improvement of coercivity and its thermal stability of hot-deformed Nd-Fe-B magnets processed by Tb<sub>70</sub>Cu<sub>30</sub> doping and subsequent Nd<sub>85</sub>Cu<sub>15</sub> diffusion

Alloying Pr-Tb-Cu diffusion source with Ni for enhancing both coercivity and corrosion resistance of Nd-Fe-B magnets

Ultrahigh coercivity and excellent thermal stability of hot-deformed Nd-Fe-B magnets by the diffusion of (Pr,Nd)-Dy-Cu-Al

Enhanced anisotropy of Pr-Nd-Fe-B HDDR magnetic powders by regulating the hydrogen decrepitated process

Effect of Nd-Ho-Al-Ga diffusion on coercivity and thermal stability of hot-deformed PrNd-Fe-B magnets

Microstructure Evolution and Coercivity Enhancement in Hot-Deformed Nd-Fe-B Magnet Processed by Pr60Tb10Cu30 Diffusion

Improvement of coercivity and its thermal stability of hot-deformed Nd-Fe-B magnets processed by Tb70Cu30 doping and subsequent Nd85Cu15 diffusion

Significantly Enhancing the Coercivity of NdFeB Magnets by Ternary Pr-Al-Cu Alloys Diffusion and Understanding the Elements Diffusion Behavior

Production of anisotropic hot deformed Nd-Fe-B magnets with the addition of Pr-Cu-Al alloy based on nanocomposite ribbon

Study on the Influence of Annealing and Ball Milling on the Magnetic Properties of HDDR Nd-Fe-B Magnetic Powder

Effective microstructure optimization and coercivity enhancement of sintered Nd–Fe–B magnet by grain boundary diffusion of Pr60Tb13Al27 alloy

Anisotropy optimization of HDDR magnetic powders by precursor alloy annealing

Coercivity enhancement of waste Nd-Fe-B magnets by Pr70Cu30 grain boundary diffusion process

Microstructure optimization and coercivity enhancement of Nd-Fe-B magnet by double-step diffusion with Pr60Cu20Al20 alloy and Tb metal