Abstract:The Ag/BiFeO3 thin films were prepared on ITO/glass substrate by in situ sol–gel method. The morphology and formation of the perovskite phase and Ag nanoparticles (NPs) were studied by XRD, SEM, and UV–Vis spectra. The doping of Ag+ ions and the formation of defects were analyzed by XPS measurement. The dielectric and magnetic properties were measured by impedance analyzer and magnetic property measurement system. Results showed that a few Ag+ ions (<7%) were doped into the bismuth ferrite lattice to substitute Bi. In addition, most of the Ag+ ions were reduced to Ag NPs in BiFeO3 thin films and the Ag NPs/BiFeO3 composite thin film was formed. The Ag+ ions doping was beneficial for not only the formation of crystalline phase of bismuth ferrite, but also the preferential orientation growth of (012) lattice plane. The Ag NPs dispersed in the thin film introduced the percolation behavior into composite the thin film, having the theoretical percolation threshold of f c = 0.131. When the volume fraction of Ag NPs is about 0.12 (Ag/Fe = 0.6). The dielectric constant of the Ag NPs/BiFeO3 thin film reached about 173, being three times as large as that of BiFeO3 thin film without Ag NPs. The minimum value of the dielectric loss was about 0.1–0.2. The typical ferromagnetic property was maintained although the magnetizations decreased a little with the increase in Ag content. The coercive force was 111Oe, showing no typical difference between the thin films with and without Ag NPs. They were beneficial to be used as a candidate in devices with both dielectric and ferromagnetic properties at the same time.

Nano Conductive Particle Dispersed Percolative Thin Film Ceramics with High Permittivity and High Tunability

Percolative Nanoparticle-Ag/pbzr0.52ti0.48o3 Composite Thin Film with High Dielectric and Ferroelectric Properties

Ag Nanoparticle Dispersed Pbtio3 Percolative Composite Thin Film with High Permittivity

Formation of Pb0.6sr0.4(Ti0.97mg0.03)O-2.97 Thin Films on Assembled Bottom Electrodes with Titanium Silicide Nanowires

Percolation-dominated Superhydrophobicity and Conductivity for Nanocomposite Coatings from the Mixtures of a Commercial Aqueous Silica Sol and Functionalized Carbon Nanotubes

The Effect of Dual Complexing Agents of Lactic and Citric Acids on the Formation of Sol-Gel Derived Ag–PbTiO3 Percolative Thin Film

Percolative Ceramic Composites with Giant Dielectric Constants and Low Dielectric Losses

Formation of Silver Nano Particles in Percolative Ag‐PbTiO 3 Composite Dielectric Thin Film

Two Stage Formation of Silver Nanoparticles in PZT Thin Films Controlled by Re-Nucleation Through Transition Phase of Ag-Pb Alloy

Formation of Ag Nanoparticles in Percolative Ag–PbTiO3 Composite Thin Films Through Lead-Rich Ag–Pb Alloy Particles Formed As Transitional Phase

Effect of Ag Doping on the Formation and Properties of Percolative Ag/BiFeO 3 Composite Thin Film by Sol–gel Method

Effect of Zn-Doping on the Tunable Behavior of (pb0.6sr0.4)tio3 Thin Films

Preparation of TiSi Nanowires by APCVD Used for Improving Dielectric Properties of PST Thin Film

Conductive HNTs-PEDOT hybrid preparation and its application in enhancing the dielectric permittivity of HNTs-PEDOT/PVDF composites

Dipole Azimuth Dependent Permittivity In Randomly And (100) Oriented (Pb,Sr) Tio3 Thin Films

Poly (vinylidene Fluoride) Based Percolative Dielectrics with Tunable Coating of Polydopamine on Carbon Nanotubes: Toward High Permittivity and Low Dielectric Loss

Strain-assisted control of high stable dielectric tunability in (100) oriented (Pb,Sr)TiO3 thin films

Alignment Of Carbon Iron Into Polydimethylsiloxane To Create Conductive Composite With Low Percolation Threshold And High Piezoresistivity

Preparation of Dielectric Tunable Zn-Doped PST Thin Films

Efficiently tuning the electrical performance of PBTTT-C14 thin film via in-situ controllable multiple precursors (Al2O3:ZnO) vapor phase infiltration

The Effect of Pre-Polarization on Dielectric Tunability of PST Thin Film