Abstract:A negatively charged monodisperse polystyrene (PSt) seed emulsion was first synthesized via batch emulsifier-free emulsion polymerization, and polyethyleneimine (PEI) aqueous solution was then added into the diluted emulsion to modify the particle surface at 25°C to prepare the positively charged PSt seed particles. Then, the core-shell PSt/TiO2 composite microspheres were obtained by adding the diluted modified PSt seed emulsion into the medium of ethanol containing certain amount of tetrabutyl titanate (TBT). Influences of pH and TBT amount on the morphology of PSt/TiO2 core-shell composite microspheres were investigated by TEM and SEM observation. Results showed that it was difficult to form PSt/TiO2 core-shell microspheres under acidic conditions, and a uniform TiO2 shell with about 29 nm in thickness was obtained when pH increased to 7. 2, and then the thickness of the TiO2 shell increased with the increase of pH value. When pH was 11. 0, the thickness of the TiO2 shell reached 70 nm, but some of the composite microspheres were partially encapsulated. With the increase of TBT amount from 0. 01 g to 0. 16 g, the thickness of PSt/TiO 2 core-shell composite microspheres gradually increased from about 0 nm to 60 nm when the amount of PSt seed emulsion was 0. 5 g (solid content was 4% by weight) and pH was controlled at 8. 5. While the TBT amount increased to 0. 32 g, the thickness of the TiO2 shell reduced to 12 nm, and the surface of the composite microspheres became rough gradually. After that, with the increase of TBT amount, the thickness of the TiO2 shell decreased, and a number of TiO2 nanoparticles appeared. The voided TiO2 microspheres were obtained by calcining the PSt/TiO2 composite microspheres at 500°C for 4 h when the thickness of TiO 2 shell in the composite microspheres reached a certain level.

PREPARATION OF PSt/TiO2 CORE-SHELL COMPOSITE MICROSPHERES VIA SURFACE MODIFICATION OF PSt SEED LATEX PARTICLES

PSt/SiO2 core-shell composite microspheres prepared by pst seed surface modification

Influences of pH and TBT amount on the morphology of PSt/TiO2 core-shell composite microspheres and void TiO2 microspheres

INFLUENCES OF Ph AND AMOUNT OF PRECURSOR ON THE MORPHOLOGY OF PSt/SiO_2 CORE-SHELL COMPOSITE MICROSPHERES

Optimising the Shell Thickness-To-Radius Ratio for the Fabrication of Oil-Encapsulated Polymeric Microspheres

Preparation of PS/TiO<sub>2</sub> core-shell microspheres and TiO<sub>2</sub> hollow shells

Preparation of PS/TiO 2 Core-Shell Microspheres and TiO 2 Hollow Shells

Preparation and Characterization of Core–shell Polystyrene–polydimethylsiloxane Particles by Seeded Polymerization

Fabrication and Characterization of Raspberry-Like Pst/Sio2 Composite Microspheres Via Miniemulsion Polymerization

Preparation of Photosensitive Monodisperse Core-Shell Raspberry-Like Pst/Pam Microspheres

Fabrication of tunable core-shell structured TiO2 mesoporous microspheres using linear polymer polyethylene glycol as templates

Synthesis of TiO2–SiO2/polymer Core–shell Microspheres with a Microphase‐inversion Method

Study on PS/TiO2 Nanocomposite Particles

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Facile preparation method of SiO2/PS/TiO2 multilayer core-shell hybrid microspheres.

Preparation and Absorption Properties of Polystyrene/ag/tio2 Multiple Coated Colloids

Preparation of Bigger Core-Shell PS/PMMA Composite Particles by Suspension-Emulsion Combined Polymerization

Preparation and Characterization of Nano-Tio2/Poly (methyl Methacrylate) Hybrid Latex by Reverse Microemulsion Method and In-Situ Polymerization

Synthesis and Characterization of N-Doped Hollow Tio2 Microspheres

Preparation and characterization of micron-sized polystyrene/polysiloxane core/shell particles

Preparation and Characterization of Core–shell Polystyrene and Polymethylsilsesquioxane Structure Latex Particles by Seeded Polymerization