Abstract:The control of the morphology of nanoparticles is a hot issue all over the world.Organic-inorganic materials can be tailor made with an infinite number of architectures and in diverse forms conveniently.A new type of organic inorganic hybrid material was reported to be synthesized by emulsion polymerization by using the monomers which contained alkoxysilane groups.However,polymerization and morphology could hardly be controled during the emulsion process, because the alkoxysilane group was easy to be subjected to hydrolysis and condensation by sol gel process which decreased the stability of the latex.In the present work, organic inorganic hybrid core shell nanoparticles were synthesized by seeded emulsion polymerization.Through morphology design, polystyrene, as seeded cores, was synthesized firstly, then 3 trimethoxysilyl propyl methacrylate (MPS) was added to form MPS styrene copolymer shell on the surface of polystyrene core. Owing to the hydrolysis condensation of organic alkoxysilane groups in MPS,the organic inorganic hybrid shell was formed through sol gel process.The core shell structure was interpreted by thermodynamical representation and characterized by transmission electron microscopy (TEM).The nonionic surfactant used would decrease the stability of the latex.In acidic condition the latex turned into gel just after the addition of MPS,while,in basic condition the particle number decreased obviously, and the latex kept almost stable in neutral condition.The higher the MPS concentration in the emulsion was,the less stability the latex had.Adding MPS continuously could keep the latex more stable and the particle size could be controlled by this method.Then, the core of this kind of hybrid nanoparticles could be dissolved to yield hollow nanocapsules, with the proportion of the void volume 40 1%.

Preparation of Sulphonate-Containing Core/shell Latex Particles Via Seeded Emulsion Copolymerization

A Novel Approach to Prepare Core/shell Polymer Latex Particles with High Sulphonate Contents

Preparation of Sulphonate-Containing Polymer Particles Via Semi-Continuous Emulsion Copolymerizaion of Styrene and Sodium Styrene Sulphonate

Preparation of Polymeric Microspheres with High Content of Sulphonate Groups

Fabrication and Characterization of Sulfonate‐containing Polystyrene/CaCO3 Core‐shell Nanoparticles

Study of the Amount of Surfactant in the Core-Shell Emulsion Polymerization

Synthesis and Redispersibility of Poly(styrene-block-n-butyl Acrylate) Core–Shell Latexes by Emulsion Polymerization with RAFT Agent–Surfactant Design

DESIGN AND CONTROL OF SOAP-FREE HYDROPHILIC-HYDROPHOBIC CORE-SHELL LATEX PARTICLES WITH HIGH CARBOXYL CONTENT IN THE CORE OF THE PARTICLES

Preparation and Structure Control of Hollow Polymer Particles——Synthesis and Effect on the Hollow Structure of the Core Latex

Preparation of Multihollow P(St–MAA) Particles by Sequence Soap-Free/soap Emulsion Polymerization and Followed by Stepwise Alkali/acid Posttreatment

Synthesis and Properties Study of the Uniform Nonspherical Styrene/Methacrylic Acid Copolymer Latex Particles

Morphology Of P(Ba-St-Daam) Latex Particles Prepared By Seeded-Emulsion Polymerization

Synthesis and properties of soap-free poly(methyl methacrylate-ethyl acrylate-methacrylic acid) latex particles prepared by seeded emulsion polymerization

Preparation of Mma-Ba-Dmaema Nanosized Latex

Tertiary Amine‐containing Poly(methyl Methacrylate–butadiene–styrene) Core/shell Nanoparticles with CO 2 ‐triggered Aggregation Behaviour

Preparation of Polyacrylate - Polysiloxane Core - Shell Latex Particles

Preparation of Bowl‐Like Polymer Particles Via Multi‐Step Emulsion Polymerization and Alkali Post‐Treatment

PREPARATION OF MULTIHOLLOW PARTICLES BY SEEDED EMULSION COPOLYMERIZASION

Preparation of Hollow Polymer Microspheres——Effect of Acid Monomer Content

Synthesis and Characterization of Hollow Polymer Latex Particles

Synthesis of organic-inorganic hybrid core-shell nanoparticles and particle size control