PSt/SiO2 core-shell composite microspheres prepared by pst seed surface modification

Guoan Chen,Wei Deng,ManYi Wang,Qingwu Zhang,Chengyou Kan

DOI: https://doi.org/10.3724/sp.j.1105.2010.09352

2010-01-01

Acta Polymerica Sinica

Abstract:A negatively charged PSt seed latex was first synthesized via batch emulsifier-free emulsion polymerization, and the PSt particles were then dispersed into the medium of ethanol and water, and γ- aminopropyltriethoxysilane (KH-550) was added to modify the particle surface at 25 °C to prepare the positively charged and silylated PSt particles. Finally, the core-shell PSt/SiO2 composite microspheres were obtained by dropwise adding tetraethoxysilane (TEOS) into the above system under alkaline condition. Influences of KH-550 amount on zeta potential of PSt seed latex, and influences of reaction time and EtOH/ H2O ratio on the morphology of PSt/SiO2 composite microspheres were investigated. Results showed that zeta potential of PSt seed latex increased with increasing the KH-550 amount, and reached its optimum value of 38 mV from-34. 5 mV when the amount of KH-550 was increased to 1/3 of PSt seed weight. In the preparation of core-shell PSt/SiO2 composite microspheres, the encapsulation ratio of SiO2 onto the modified PSt particles increased with the increasing reaction time, and maximum value of 97. 9% achieved when the reaction time prolonged to 24 h; With the decrease of EtOH/H2O, the number of SiO2 nanoparticles absorbed onto the composite microspheres decreased, and the uniform core-shell PSt/SiO2 composite microspheres with the shell thickness about 35 nm were obtained in the medium with EtOH/H2O weight ratio of 60/28. 5.