Abstract:High strength-elongation synergy and its dependence on microstructure are the eternal themes of metallic materials including Ti alloys. In this study, the relationship between the microstructure evolution and mechanical properties of the Ti-25Zr-4Al-1.5Mn (TZAM, wt. %) near-α Ti alloy was systematically investigated after hot rolling at temperatures ranging in the whole solid solution region. The content of primary α phase decreased gradually with the increasing of rolling temperature. An excellent comprehensive mechanical properties with a yield strength of 1055±10 MPa and a total elongation of 23.6±0.6% were obtained for the specimen after rolling at 750 °C (single α phase temperature region). This great strength-elongation synergy is mainly due to the synthetic action of substructure strengthening, dislocation strengthening, basal random heterogeneity (BRH) texture, and suitable content of β phase. The α" martensitic phase was formed after rolling at temperatures of 800 and 850 °C (α + β two-phase temperature region), resulting in a significant decrease in yield strength. However, remarkable work hardening with a rate of approximately 10 GPa occurred in both specimens. The whole evolution process of primary α grains, namely dynamic recovery and recrystallization during hot-rolled is deeply discussed. When the rolling temperature increased to 900 °C (single β phase temperature region), the dominated acicular α´ martensitic phase with high dislocation density resulted in an ultra-high strength (1264±12 and 1488±11 MPa for yield and tensile strength respectively) at the expense of plasticity. These findings revealed the microstructure evolution and its relationship to the mechanical properties of a TiZr-based alloy after the thermomechanical processing and helped to understand deeply the theory of metallic strengthening and elongation.

Quantitative microstructural analysis of Ti-6Al-4V alloy after hot forging process by means of stereological morphometry

Constitutive Model and Microstructure Evolution of a Novel TG6 High-Temperature Titanium Alloy during Hot Deformation

The Effect of the Forging Process on the Microstructure and Mechanical Properties of a New Low-Cost Ti-5Al-1.5Mo-1.8Fe Alloy

Crystallographic orientation and slip behavior of powder metallurgy Ti–6Al–4V via multi-directional forging

Miniaturised experimental simulation and combined modelling of open-die forging of Ti-6Al-4V titanium alloy

Research on hot deformation behavior and numerical simulation of microstructure evolution for Ti–6Al–4V alloy

Microstructure Regulation and Strength-Elongation Synergy of the Near Alpha TZAM Alloy Via Thermomechanical Processing

Hot Deformation Behavior and Microstructure Evolution Mechanisms of Ti6Al4V Alloy under Hot Stamping Conditions

Rheology of Ti-6Al-4V alloy under non equilibrium conditions during β forging

Mechanical and Physical Characterizations of a Three-Phase TiAl Alloy during Near Isothermal Forging

Quantitative analysis on microstructure characteristic of pre-strained β-solidified TiAl alloy during post-heat treatment

Microstructure and texture of Ti-6Al-4V alloy deformed by rotary forging at elevated temperatures

Microstructure Evolution and Deformation Mechanisms of As-Cast Antibacterial Ti6Al4V-5Cu Alloy for Isothermal Forging Process

Effects of the cooling rate on mechanical properties and microstructure of near- α Ti-6Al-3Zr-2Nb-Mo alloy

Optimization of hot deformation parameters for multi-directional forging of Ti65 alloy based on the integration of processing maps and finite element method

Constitutive modeling and microstructure research on the deformation mechanism of Ti-6Al-4V alloy under hot forming condition

Achieving high strength-ductility synergy in a hierarchical structured metastable β-titanium alloy using through-transus forging

Drastic enhancement in hot-workability and microstructural refinement of TiAl alloys via martensitic transformation: A comparative study

Constitutive Model and Microstructure Evolution of Ti65 Titanium Alloy

Influence of Forging Temperature on the Microstructures and Mechanical Properties of a Multi-Directionally Forged Al–Cu–Li Alloy

Microstructure evolution and prediction of TC4 titanium alloy during isothermal forging