Abstract:Objective. To evaluate the electrochemical properties, biological response, and surface characterization of an electrodeposited Platinum-Iridium (Pt-Ir) electrode coating on cochlear implants subjected to chronic stimulation in vivo. Approach. Electrochemical impedance spectroscopy (EIS), charge storage capacity (CSC), charge injection limit (CIL), and voltage transient (VT) impedance were measured bench-top before and after implant and in vivo. Coated Pt-Ir and uncoated Pt electrode arrays were implanted into cochlea of normal hearing rats and stimulated for ~4 h d, 5 d week−1 for 5 weeks at levels within the normal clinical range. Neural function was monitored using electrically-evoked auditory brainstem responses. After explant, the electrode surfaces were assessed, and cochleae examined histologically. Main results. When measured on bench-top before and after stimulation, Pt-Ir coated electrodes had significantly lower VT impedance (p < 0.001) and significantly higher CSC (p < 0.001) and CIL (p < 0.001) compared to uncoated Pt electrodes. In vivo, the CSC and CIL of Pt-Ir were significantly higher than Pt throughout the implantation period (p= 0.047 and p< 0.001, respectively); however, the VT impedance (p= 0.3) was not. There was no difference in foreign body response between material cohorts, although cochleae implanted with coated electrodes contained small deposits of Pt-Ir. There was no evidence of increased neural loss or loss of neural function in either group. Surface examination revealed no Pt corrosion on any electrodes. Significance. Electrodeposited Pt-Ir electrodes demonstrated significant improvements in electrochemical performance on the bench-top and in vivo compared to uncoated Pt. Neural function and tissue response to Pt-Ir electrodes were not different from uncoated Pt, despite small deposits of Pt-Ir in the tissue capsule. Electrodeposited Pt-Ir coatings offer promise as an improved electrode coating for active neural prostheses.

Platinum Wire Implants Coated with PEDOT/carbon Nanotube Conducting Polymer Films in the Brain of Rats: A Histological Evaluation

PEDOT/MWCNT Composite Film Coated Microelectrode Arrays for Neural Interface Improvement

In Vivo Electrochemical Analysis of a PEDOT/MWCNT Neural Electrode Coating

Long term performance of porous platinum coated neural electrodes

Electrodeposited Polypyrrole/carbon Nanotubes Composite Films Electrodes for Neural Interfaces.

Electrodeposited PEDOT:BF4 Coatings Improve Impedance of Chronic Neural Stimulating Probes In Vivo

Nanostructured PEDOT Coatings for Electrode-Neuron Integration

Evaluation of poly(3,4-ethylenedioxythiophene)/carbon nanotube neural electrode coatings for stimulation in the dorsal root ganglion

Surface Modification of Neural Probes with Conducting Polymer Poly(hydroxymethylated-3,4-ethylenedioxythiophene) and Its Biocompatibility

Biocompatibility and magnetic resonance imaging characteristics of carbon nanotube yarn neural electrodes in a rat model

Magnetically Compatible Brain Electrode Arrays Based on Single-Walled Carbon Nanotubes for Long-Term Implantation

Nanofibrous PEDOT-Carbon Composite on Flexible Probes for Soft Neural Interfacing

Coating of Neural Electrodes with Platinum Nanoparticles Reduces and Stabilizes Impedance In Vitro and In Vivo in a Rat Model

Electrochemical and biological characterization of thin-film platinum-iridium alloy electrode coatings: a chronic in vivo study

Platinum‐Iridium Alloy Nanoparticle Coatings Produced by Electrophoretic Deposition Reduce Impedance in 3D Neural Electrodes

Layered carbon nanotube-polyelectrolyte electrodes outperform traditional neural interface materials

Evaluation of chronically implanted subdural boron doped diamond/CNT recording electrodes in miniature swine brain

Electrodeposition of alginate with PEDOT/PSS coated MWCNTs to make an interpenetrating conducting hydrogel for neural interface

Poly(vinyl Alcohol)/poly(acrylic Acid) Hydrogel Coatings for Improving Electrode–neural Tissue Interface

PEDOT:PSS-coated platinum electrodes for neural stimulation

Fabrication of Vertically Aligned PEDOT Nanotube Arrays on Microelectrodes to Interface Neurons