Synthesis of Cross-linked Carboxyl Modified Polyvinyl Alcohol and its Application in Selective Adsorption Separation of Cu(II) from Cd(II) and Ni(II)
Lelin Zeng,Feixiang Zhou,Rong Hu,Wanyun Xie,Guoxiang Wang,Caixia Yang,Enxiang Liang,Wenyuan Xu,Bart Van der Bruggen
DOI: https://doi.org/10.1007/s10924-020-01847-z
IF: 4.705
2020-08-12
Journal of Polymers and the Environment
Abstract:A cross-linked copolymer (XL-P(AA-co-VAc)) of vinyl acetate and acrylic acid was prepared using azobisisobutyronitrile as initiator and N,N’-methylenebisacrylamide as crosslinker. Then, XL-P(AA-co-VAc) was reacted with ethanol to prepare a crosslinked carboxyl modified polyvinyl alcohol (XL-P(AA-co-VA)). The as-prepared XL-P(AA-CO-VA) hydrogel was characterized by FTIR, XRD, SEM and BET, and investigated as an selective heavy metal ion adsorbent. The adsorption characteristics of the XL-P(AA-CO-VA) hydrogel were studied with a aqueous solution containing ternary metal ions Cu(II), Cd(II) and Ni(II). It was found that XL-P(AA-CO-VA) can selectively adsorb Cu(II) in competition with Cd(II) and Ni(II), and the selectivity coefficients of 48 (βCu(II)/Cd(II)) and 80 (βCu(II)/Ni(II)) were obtained. The kinetics were demonstrated to match well with the pseudo-second order kinetics model with the rate constants (K2, g/(mg•min)) of 3.71✕10− 4, 0.0011 and 0.0015 for Cu(II), Cd(II) and Ni(II), respectively. The equilibrium adsorption of Cu(II) to the XL-P(AA-CO-VA) hydrogel follows the Langmuir adsorption model with qmax of 41.27 mg/g and KL of 0.94 L/mg. The thermodynamic studies indicate that ΔG0 was negative and increased with temperature, and the adsorption process of XL-P(AA-CO-VA) for Cu(II) ion was spontaneous and exothermic. ΔH and ΔS were − 56.57 kJ/mol and − 171.18 J·(mol·K)−1, respectively. The XL-P(AA-CO-VA) hydrogel is of interest for the selective separation of Cu(II) from industrial wastewater containing Cd(II) and Ni(II).
engineering, environmental,polymer science