Fe_3O_4/Acrylate-based Magnetic Microparticles:Preparation and Adsorption Performance Toward Hg~(2+),Cu~(2+) and Ni~(2+)

Limin Zhou,Zhirong Liu

2007-01-01

Abstract:A novel Fe_3O_4/acrylate-based magnetic adsorbent were prepared by suspension polymerization using divinybenzene as a crosslinker.The parameters for polymerization were n(methyl acrylate)∶n(divinybenzene)=17∶1,w(initiator)=1%,reaction temperature 75～80 ℃ and reaction time 6 h.This adsorbent was characterized by XRD,IR,TGA etc.Moreover,the adsorption performance of the adsorbent towards metal ions was investigated.The results showed that the diameter of the magnetic adsorbent was 35～55 μm and the content of Fe_3O_4 was 18%.The adsorption capacity increased with increasing pH.The maximum adsorption capacity(q_m) was 2.3 mmol/g for Hg~(2+),2.2 mmol/g for Cu~(2+) and 1.1 mmol/g for Ni~(2+).The adsorption rate constant calculated by Lagergrent equation was 0.023 min~(-1) for Hg~(2+),0.034 min~(-1) for Cu~(2+) and 0.036 min~(-1) for Ni~(2+).Regeneration of the adsorbent was achieved using 1 mol/L H_2SO_4 or 0.5 mol/L HNO_3.