Effect of Nd2O3 doping content on the properties of CeO2-ZrO2-Al2O3

Na Peng,Shanhu Chen,Jufa Zhou,Yaoqiang Chen,Maochu Gong
DOI: https://doi.org/10.3724/SP.J.1077.2012.11810
IF: 1.292
2012-01-01
Journal of Inorganic Materials
Abstract:A series of CeO2-ZrO2-Al2O3 (CZA) mixed oxides with Nd2O3 contents 0-13wt% were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), N-2 adsorption-desorption at low temperature, oxygen pulsing technique (OSC). H-2-temperature programmed reduction (H-2-TPR) and scanning electrical microscope (SEM). The results show that the solubility limit of Nd2O3 in the CZA solid solution is about 10wt%. With excessive Nd dopant, the single phase will separate resulting in the formation of Nd0.5Ce0.5O1.75 phase. Furthermore, the proper addition of Nd to CZA solid solution effectively restrains the sintering of oxide particles and greatly improves the thermal stability and redox property of the materials. When the doping amount of Nd2O3 in CZA solid solution is 10wt%, the sample has the best textural stability i.e. after calcination at 1000 degrees C for 5 h, the specific surface area and pore volume achieve 97.14 m(2)/g and 0.44 mL/g, respectively. For the CZA sample prepared with 7wt% Nd2O3 in CZA solid solution, the OSC is the highest in all samples, reaching 938.01 mu mol/g and 821.72 mu mol/g after calcination at 600 degrees C and 1000 degrees C, respectively. Meanwhile, the mobility of hulk oxygen is the strongest and the sample has optimal reducibility at low temperature. After aging, the reduction peak temperature can be increased from 465 degrees C to 483 degrees C. SEM image shows that all the prepared CZA samples have spherical particles and Nd2O3 can effectively prevent the agglomeration of particles in the process of high-temperature calcination.
What problem does this paper attempt to address?