Research Progress in Degradation Process of Anti-corrosion Coatings in Water Containing Environments

Zhang Lixin

2012-01-01

Abstract:In this paper,the degradation process and the relevant mechanism of anti-corrosion coatings with and without artificial defects in water containing environments were summarized. The factors affecting the cathodic delamination were discussed,the mechanism of cathodic delamination and blistering were elaborated.

What problem does this paper attempt to address?

Failure Behavior of Protective Organic Coatings under Corrosive Conditions

XC Zhang,BS Xu,HD Wang,YX Wu

2004-01-01

Abstract:Recent research activities on the formation of micro-defects and porosity in organic coatings were reviewed. The mechanisms of aggressive ionic conduction through organic coatings were analyzed. The micro-mechanisms for the failure behavior of coatings under corrosive environments were discussed in detail. These mechanisms included blistering (i.e. osmotic blistering, anodic blistering and cathodic blistering) in the coating, wet-adhesion loss at the substrate/coating interface, cathodic delamination of coating from the substrate. Based on these researches, it was found that the failure behavior of organic coatings is closely related to the micro-defects in coatings, regardless of the failure mode. Additionally, the general failure mode of a coating system was proposed to interpret the failure behavior of organic in corrosion environments. The topics discussed can provide some insights into the development of a methodology for designing fail-safe coating systems.
Coating Deterioration and Underlying Metal Corrosion Processes in Water-Line Area: Role of DACs

Zhiwei Chen,Wei Zhang,Yi Zhan,Bing Lei,Tianying Sun,Weihua Li

DOI: https://doi.org/10.3390/coatings10070684

IF: 3.236

2020-07-16

Coatings

Abstract:Water-line corrosion is a highly concentrated type of localized corrosion. The conventional single electrode method is limited in its ability to obtain the kinetic information of the corrosion occurrence and development processes. Herein, the coating deterioration and underlying metal corrosion processes in water-line area were studied by a small wire beam electrode to monitor the current density distribution. The distance between each electrode was very small (interval: 0.3 mm), thus facilitating it to approach the practical metal component with a continuous surface. The results showed that cathodic and anodic sites tended to be weak points of the coating at the initial stage. With the continuous degradation of the coating, the cathodic zone tended to occur in the above the anodic zone due to the effect of differential aeration cells (DACs). Subsequently, the cathodic zone expanded to the waterline and the polarity reversed to the anodic zone, causing the coating to peel and blister continuously from the bottom up. When the cathodic zone extended to the gas phase area above the water line, this area became the strongest cathodic zone under the action of the thin liquid film, thus significantly accelerating the corrosion of the base metal at the bottom. The present study aims to achieve an in-depth understanding of coating deterioration and underlying metal corrosion processes in the water-line area, providing a new means of directly visualizing the role of DACs played in water line corrosion.

materials science, multidisciplinary,physics, applied, coatings & films
PROGRESS IN EFFECT OF COATING DEFECTS ON CORROSION BEHAVIOR OF METAL SUBSTRATE BENEATH CONTINGS

刘斌,李瑛,林海潮,曹楚南

DOI: https://doi.org/10.3969/j.issn.1002-6495.2001.02.012

2001-01-01

Abstract:Effect of coating defect on the corrosion behavior of metalsubstrate the relevant methods applied in this research field have been reviewed. In this study field, one of the prime problems is how to characterize the porosity of coatings. Many physical and chemical study methods, such as"chamber test","immersion test"and"electrochemical test"have been used. However, those methods are not efficient enough to reveal the defects randomly distributed in coatings. Statistical method has been pointed out to be a suitable method for studying the characteristics of defect. The relationship among the characteristics of defects, the diffusion behavior of corrosive agents through coatings and the corrosion behavior of metal beneath the coatings is another unsolved problem. Methods to solve these problems were also proposed in this paper.
Research Progress of Marine Anti-corrosion and Wear-resistant Coating

Wenle Pei,Xiaoliang Pei,Zhuangzhuang Xie,Jianmei Wang

DOI: https://doi.org/10.1016/j.triboint.2024.109864

IF: 5.62

2024-06-08

Tribology International

Abstract:The marine environment has caused significant economic losses to marine engineering machinery, and the exploitation of simple, environmentally friendly, economical, mechanically durable marine protective coatings is imminent. This article provides a comprehensive review of the recent research advancements in marine metal protective coatings, such as superhydrophobic coatings, micro-arc oxidation coatings, laser cladding coatings, and graphene nano-anticorrosion coatings. The review explores their respective anticorrosion strategies, anticorrosion and wear-resistant mechanisms, preparation processes, and influencing factors. Ultimately, it summarizes the challenges in the practical application of marine coatings in marine corrosion protection, which provides an outlook on the future direction of coating development. The application of marine anticorrosion and wear-resistant coatings provides reliable protection to ensure the regular operation of marine resource development facilities.

engineering, mechanical
Modification, Degradation and Evaluation of a Few Organic Coatings for Some Marine Applications

Guang-Ling Song,Zhenliang Feng

DOI: https://doi.org/10.3390/cmd1030019

2020-12-21

Corrosion and Materials Degradation

Abstract:Organic coatings for marine applications must have great corrosion protection and antifouling performance. This review presents an overview of recent investigations into coating microstructure, corrosion protection performance, antifouling behavior, and evaluation methods, particularly the substrate effect and environmental influence on coating protectiveness, aiming to improve operational practice in the coating industry. The review indicates that the presence of defects in an organic coating is the root cause of the corrosion damage of the coating. The protection performance of a coating system can be enhanced by proper treatment of the substrate and physical modification of the coating. Environmental factors may synergistically accelerate the coating degradation. The long-term protection performance of a coating system is extremely difficult to predict without coating defect information. Non-fouling coating and self-repairing coatings may be promising antifouling approaches. Based on the review, some important research topics are suggested, such as the exploration of rapid evaluation methods, the development of long-term cost-effective antifouling coatings in real marine environments.
Preparation and Corrosion Performance of Electrophoretic Epoxy Coatings Doped with ZrO2

Mei GAO,Liankui WU,Jiming HU

DOI: https://doi.org/10.11903/1002.6495.2014.154

2015-01-01

Abstract:在电泳清漆环氧树脂中掺杂硝酸锆(Zr(NO3)4·5H2O),采用一步电泳法制备ZrO2掺杂改性的阴极电泳漆涂层,用于镀锌钢的腐蚀防护。红外测试表明,硝酸锆水解产物ZrO2与环氧树脂粒子共沉积构成阴极电泳涂层,并在涂层/金属界面发生富集。电化学阻抗谱、盐水浸泡和电化学扫描显微镜等结果表明,硝酸锆掺杂的电泳漆涂层防腐蚀性能得到大幅度提高。这可能是由于一方面掺杂形成的ZrO2填补了涂层本体的微孔缺陷,另一方面ZrO2在涂层与金属界面形成的富集层提高了涂层与金属之间的结合力。
Degradation Damage of Stress Corrosion in Epoxy Zinc-Rich Coating/Steel Substrate Systems

Hua Zhang,Lei Yang,Qi Liang Li,Xue Ming Huang,Yi Xuan Cao

DOI: https://doi.org/10.1061/(asce)mt.1943-5533.0004738

IF: 3.2

2023-05-01

Journal of Materials in Civil Engineering

Abstract:In this paper, the corrosion resistance and mechanical properties of a coating/steel substrate system were investigated under the coupling action of the corrosive environment and load. At first, the stress corrosion tests were carried out on the coating/steel substrate specimens. Then, nanoindentation tests were used to study the elastic modulus of the coating before and after stress corrosion tests. After that, tensile tests were performed on the specimens before and after stress corrosion tests. In the tensile testing process, the evolution law of surface strain was studied by a digital image correlation method. Further, the cracking characteristics and fracture toughness of the coating/steel substrate system in the corrosion process were generated. Test results indicate that the elastic modulus of the coating/steel substrate system continuously decreases with increasing stress level. In the meantime, the critical cracking strain and fracture toughness of the coating/steel substrate system also decrease with increasing stress level. The coupling effect of the external load and corrosive environment greatly accelerate the corrosion process of the coating/steel substrate system.

construction & building technology,materials science, multidisciplinary,engineering, civil
Corrosion resistances of metallic materials in environments containing chloride ions: A review

Xian-man ZHANG,Zai-yu CHEN,Hong-feng LUO,Yu-liang ZHAO,Zi-cheng LING,Teng ZHOU

DOI: https://doi.org/10.1016/s1003-6326(22)65802-3

IF: 3.752

2022-02-01

Transactions of Nonferrous Metals Society of China

Abstract:Corrosion, more specifically, pitting corrosion happening extremely in marine environments, leads to lifespan of materials drastically decreasing in service, which causes enormous economic loss and even environmental disaster and casualties. In the past decade, increasing efforts have been made to study the corrosion behaviors of materials in chloride-containing aqueous environments. Herein, this work provides an overview of recent progress in understanding the degradation mechanism and improving the corrosion resistance and corrosion-wear resistance of materials from bulk metal to surface treatment involving organic coating, metal and its alloy or compound coating. The particular emphasis is given to the periodic layered structures (PLSs), whose anti-corrosion properties outperformed others to some extent, wherever in terms of bulk metal or surface treatment, regardless of aggressive environment (corrosion or corrosion-wear conditions). Numerical simulation based on kinds of models at different scales is introduced to deeply understand the process of corrosion and/or corrosion-wear in chloride-containing aqueous environment. Combined experimental result with numerical simulation, the micro-galvanic corrosion dominated degradation mechanism of PLSs is critically analyzed. Types of setups to realize corrosion-wear in laboratory are also summarized. At last, future research and development are prospected, offering to develop a basic application of PLSs designed by corrosion protection methodology in the near future.

metallurgy & metallurgical engineering
Progress in corrosion problem in process of supercritical water oxidation

Bei-lin ZUO,Tao FANG,Li-xun ZHU,Jian-feng DU,Wei-hai ZHANG

DOI: https://doi.org/10.16606/j.cnki.issn0253-4320.2011.s2.029

2011-01-01

Abstract:Supercritical water oxidation is a new technology for treating organic pollutants and wastewater.When the temperature and pressure exceeds the critical value of water(Tc=374.2℃ and Pc=22.12 MPa),the physical properties of water changes tremendously.In details,supercritical water can dissolve some materials generally insoluble in liquid water,especially some organic chemicals can be oxidized and decomposed efficiently in supercritical water,which is regarded as a kind of ideal homogeneous medium.Although the technology has many advantages,the problem of corrosion seriously hinders the industrial application of the technology.This paper reviews the research progress on the corrosion problem occurring in the process of supercritical water oxidation.The relevant parameters are analyzed for reducing the corrosion to the materials of equipment.Beyond,this work reviews some corrosion-resistance materials used in the process of supercritical water oxidation in order to develop better equipments against corrosion in different media.
Synergistic effects of fluid flow and hydrostatic pressure on the degradation of epoxy coating in the simulated deep-sea environment

Fandi Meng,Li Liu,Erhai Liu,Hongpeng Zheng,Rui Liu,Yu Cui,Fuhui Wang

DOI: https://doi.org/10.1016/j.porgcoat.2021.106449

IF: 6.6

2021-10-01

Progress in Organic Coatings

Abstract:The anticorrosion performance of epoxy varnish coating/steel systems under a simulated deep-sea fluid-pressure (FP) environment was studied using physical performance tests, electrochemical measurements and finite element modeling. The results show that fluid flow provides an initial kinetic energy to water, and the hydrostatic pressure difference reduces the energy barrier for water absorption, leading to premature corrosion of the coated steel under FP condition. Detachment of polymer pieces from the coating surface and large areas of blistering are found to occur under the synergistic effects of fluid and pressure, which can be attributed to the release of internal stress at coating defects.

materials science, coatings & films,chemistry, applied
A Comprehensive Review on Smart Anti-Corrosive Coatings

Gan Chen,Zhenxiao Bi,Shuai‐Hua Wang,Jianguo Liu,Xing Xiao,Zili Li,Bingying Wang

DOI: https://doi.org/10.1016/j.porgcoat.2020.105821

IF: 6.6

2020-01-01

Progress in Organic Coatings

Abstract:Smart anticorrosive coatings have better anticorrosion ability than traditional anticorrosive coatings. This is attributed to the development of active protection performance in the smart anticorrosive coating based on the passive barrier of the traditional coating. Smart anticorrosive coating can effectively respond to environmental changes, heal coating defects, and prevent further corrosion. In this study, the application prospects of smart anticorrosive coatings for protection of metal corrosion are reviewed from two aspects of extrinsic and intrinsic self-healing. First, the related concepts of healing due to coating are introduced. Second, the development of nano-container, anticorrosion performance, existing problems, and optimization measures of the extrinsic healing smart anticorrosive coating are introduced. Third, the mechanism, anti-corrosion performance, existing problems, and optimization measures of intrinsic healing smart anticorrosive coating are summarized. Finally, the development direction of smart anticorrosive coating is put forward, and the possible application prospects of these smart coatings to attain a long-term effect in the future are discussed.
The corrosion deterioration of reinforced passivation Film: The impact of defects

Dongshuai Hou,Kaixuan Zhang,Fen Hong,Shenrong Wu,Zhao Wang,Mengmeng Li,Muhan Wang

DOI: https://doi.org/10.1016/j.apsusc.2021.152408

IF: 6.7

2022-04-01

Applied Surface Science

Abstract:In reinforced concrete, the first step of steel corrosion is the structural deterioration of the passivation film that can prevent further corrosion. Due to the nanoscale properties of passivation film structure, understanding its deteriorated mechanism is still a challenge. Here, the nano-process of passivation film corrosion is revealed by employing reactive molecular dynamics. It is found that the layer structure of γ-FeOOH in passivation film has a strong resistance to corrosion in solution, which corresponds to its high corrosion prevention. The perfect structure of γ-FeOOH is hard to deteriorate. However, introducing the defects in the passivation film structure can facilitate corrosion deterioration. By introducing the [001] and [100] defects in the γ-FeOOH structure, the interaction between passivation film and solution is increased. But only the [100] defects can lead to structural deterioration. The difference between the [001] and [100] defects are originated from the competitive effects between the O atoms in γ-FeOOH and the O atoms in water on Fe atoms. The γ-FeOOH structure deteriorates when the O atoms in water are winning. Moreover, the nano products of γ-FeOOH deterioration are also observed. This work reveals the fundamental deteriorated process of passivation film and is also the first step to exploring the corrosion of steel bars in the engineering environment.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Comparative Studies on the Deterioration Process of Organic Coatings under Immersed and Cyclic Wet-Dry Conditions by EIS

LI Yu-nan,WANG jia,ZHANG Wei

DOI: https://doi.org/10.13208/j.electrochem.2010.04.009

2010-01-01

Abstract:Under the immersed and wet-dry cyclic conditions,the deterioration processes of the organic coatings on carbon steel surface have been comparatively studied by using electrochemical techniques.The wet-dry cycles were carried out in the alternating conditions of 12 h by immersing in a 3.5% sodium chloride solution and drying at 25 ℃ and 50% RH.Coating resistance,Rf,coating capacitance,Cf,and double layer capacitance,Cd,were monitored continuously and separately under above two conditions.The percentages of the intenfacial active area,Aw,were estimated from the obtained double layer capacitance,Cd.According to the EIS characteristics,the entire deterioration processes under above two mentioned conditions can be divided into three main stages,consisting of the medium penetration into coatings,corrosion initiation and corrosion extension underlying coatings.Comparing with the immersed,the cyclic wet-dry greatly accelerated the corrosion initiation stage,but decelerated the medium penetration and corrosion extension underlying coatings stages.The acceleration mechanism of the coatings and underlying metal corrosion under wet-dry cycles was discussed based on above results.
Corrosion Behavior and Mechanism of WC-12Co Coating in Salt Spray Environment

Fei Xu,Tian Liu,Guo-hao Yang,Yong Tan,Hai-jing Sun,Jie Sun

DOI: https://doi.org/10.1007/s11665-024-09186-z

IF: 2.3

2024-01-30

Journal of Materials Engineering and Performance

Abstract:WC-based wear-resistant coatings are usually corroded in salt spray environment, which seriously affects their performances. In this work, the corrosion behavior and corrosion mechanism of WC-12Co coating exposed to salt spray conditions were studied. The results showed that W 2 C and W phases were produced on the surface of WC-12Co coating via decarburization during spraying and participated in the corrosion process of the coating. The existence of pores was an important factor in the occurrence and development of coating corrosion. The Co in the WC-12Co coating was corroded to the most extent, followed by other components in the coating.

materials science, multidisciplinary
From Wet to Protective: Film Formation in Waterborne Coatings

Abolfazl Arjmandi,Huichao Bi,Stefan Urth Nielsen,Kim Dam-Johansen

DOI: https://doi.org/10.1021/acsami.4c09729

IF: 9.5

2024-10-22

ACS Applied Materials & Interfaces

Abstract:The importance of anticorrosive coatings cannot be overstated, as they play a vital role in safeguarding assets and infrastructure across various industries. Within this context, the emergence of waterborne (WB) coatings stands out for their paramount significance, offering a sustainable alternative to traditional solvent-based (SB) coatings and addressing pressing environmental concerns. Despite their eco-friendliness, the complexity of their film formation mechanism and the lack of...

materials science, multidisciplinary,nanoscience & nanotechnology
The Study Development of Corrosion in Molten Zinc Bath

MA Jing,WANG Jun,LU Heping,SUN Baode,LIN Jinping

DOI: https://doi.org/10.3321/j.issn:1005-023x.2007.06.024

2007-01-01

Abstract:In this paper,the protection application of parts suffered from molten metal corrosion in hot dip galvanizing bath is analysed.The studies at present can be divided into two sorts,choices of material and surface treatment.For the high cost of whole material and the relative poor corrosion resistance to molten zinc,more attention has been paid to surface treatment.Surface treatment includes boronizing by diffusion,thermal spraying coating,surface coating and surface insulating which have their characteristics respectively.Finally the corrosion mechanism of material in molten metal is summarized.Moreover the development direction in future is proposed.
Degradation Behavior of Arc-Sprayed Zinc Aluminum Alloy Coatings for the Vessel Yongle in the South China Sea

Guo-Sheng Huang,Zi-Lin Li,Xiao-Shuo Zhao,Yong-Lei Xin,Li Ma,Ming-Xian Sun,Xiang-Bo Li

DOI: https://doi.org/10.3390/coatings13071139

IF: 3.236

2023-06-24

Coatings

Abstract:Since thermally sprayed zinc and aluminum coatings were invented 100 years ago, they have realized extensive industrial applications for steel structure protection in a variety of fields for nearly 100 years and have been proven to be effective and reliable. However, it has seldom been reported in the ship industry in China since many workers worry about the risk of rapid corrosion, especially in harsh environments such as the South China Sea. In this paper, three kinds of arc-sprayed zinc aluminum coatings were tested to choose the best coating system for application on the research vessel Yongle by electrochemical behavior and a long-term atmospheric exposure experiment. The variation of the corrosion rate and the bonding strength was used to clarify the long-term protection performance. The results show that Zn15Al has the lowest corrosion (Rp larger than 2200 Ω·cm2) among the three kinds of coatings and has a bonding strength larger than 6.38 MPa after a 5 year test. The performance of the coatings in the South China Sea indicates that they can provide excellent protection for the hull above the waterline of the Yongle vessel in the 3 year test. It could be predicted that thermally sprayed zinc aluminum coating has vast application potential in the South China Sea due to its excellent anticorrosion performance.

materials science, multidisciplinary,physics, applied, coatings & films
Effect of Chromate on the Electrochemical Behavior of Sintered Zn–Al Coating in Seawater

Huili Hu,Ning Li,Yongming Zhu

DOI: https://doi.org/10.1016/j.surfcoat.2008.06.084

IF: 4.865

2008-01-01

Surface and Coatings Technology

Abstract:To improve the anticorrosion resistance of chromium-free Zn–Al sintered coating, characteristics of chromate on zinc–aluminum–chromium were studied by electrochemical methods. Depth profiles of elements were obtained by glow discharge spectrum (GDS) and X-ray photoelectron spectroscopy (XPS) was used to analyse the chemical states of main elements in Zn–Al coatings. Corrosion behaviors of steel samples coated with chromium-free Zn–Al and zinc–aluminum–chromium exposed to seawater were investigated by using electrochemical impedance spectroscopy (EIS) measurement. Both in open circuit potential and EIS monitoring self-healing phenomena of chromate were obviously observed. The self-healing function endows zinc–aluminum–chromium coating with better anticorrosion performance. Electrochemical analysis show that self-healing action of coatings is missing when replace chromate with molybdate and silane.
Development of Novel Environment-friendly Antifouling Materials

Zhang-ji YE,Shan-shan CHEN,Chun-feng MA,Jian-hua WU,Guang-zhao ZHANG

DOI: https://doi.org/10.16490/j.cnki.issn.1001-3660.2017.12.012

2017-01-01

Surface Technology

Abstract:Development history and antifouling mechanisms of marine antifouling materials were briefly reviewed, and the latest research progress of novel environmental-friendly antifouling materials was presented. After tributyltin-containing self-polishing copolymer (SPC) coatings were prohibited, copper, zinc and silyl acrylate polymers-based coatings have been widely used. In order to further improve the antifouling properties and environmental protection performance, research is now focusing on grafted antifouling functional group materials, biodegradable macromolecule-based antifouling materials, main chain degradable self-polishing antifouling materials, anti-drag antifouling materials and biomimetic antifouling materials. Grafting methods and antifouling effects of several antifouling functional groups such as Schiff base, glyphosate and benziso-thiazolinone were introduced. It was pointed out that such methods could improve utilization ratio of antifoulant and gain a steady release rate of antifoulant. However, such problems as reduced antifouling capacity due to grafting modification and complex synthesis process should be solved to apply such methods. Moreover, structure and synthesis methods of biodegradable macromolecule-based antifouling materials, especially main chain degradable and side chain hydrolysable were introduced em-phatically. As these hydrolysable/degradable resins exhibited good mechanical properties and hydrolysis controlled performance, the anti-fouling coatings as-prepared could release antifoulant steadily even in static state. Therefore, the resins could be used to develop novel main chain degradable self-polishing antifouling coatings, so as to improve durability of the coatings in static state, the resins had good application prospects. Methods of reducing surface roughness of the antifouling coatings after hydro-lysis such as macromolecule resin modification were introduced as well. Such anti-fouling coatings exhibited good anti-drag re-sistance. Finally, the progress of biomimetic antifouling materials was introduced.
Experimental study and finite element analysis of degradation behavior of epoxy zinc-rich coating system under stress corrosion

Hua Zhang,Xueming Huang,Lei Yang,Xiao Chen,Jiakun Lu

DOI: https://doi.org/10.1080/01694243.2023.2241206

IF: 2.431

2023-08-13

Journal of Adhesion Science and Technology

Abstract:This paper aims to study the effect of stress corrosion on the electrochemical behavior and corrosion mechanism of epoxy zinc-rich coating/steel substrate. The electrochemical impedance spectroscopy (EIS) was applied to characterize the corrosion behavior of the system under different stress conditions (σ1 = 0MPa; σ2 = 120MPa; σ3 = 180MPa and σ4 = 240 MPa), and appropriate equivalent circuits were established. Additionally, the von Mises stress distribution and potential distribution around the pitting pit at the coating-substrate interface were quantified by means of finite element analysis. The approach used different tensile strains and the depths of the pitting pit to relate the corrosion current density and corrosion rate to the corrosion process. The EIS results demonstrate that, given the same time, the failure time of the epoxy zinc-rich coating/steel substrate system with 240 MPa is shortened by 27.8% compared to the system without stress. Meanwhile, the finite element model confirms that the uneven potential distribution around the pitting pit is responsible for coating failure. In-depth profile of the corrosion rate shows an increasing trend over the distance from the opening. Then this local corrosion acceleration will cause further stress concentration, which in turn accelerates the corrosion process of the system.

materials science, multidisciplinary,engineering, chemical,mechanics

Research Progress in Degradation Process of Anti-corrosion Coatings in Water Containing Environments

Failure Behavior of Protective Organic Coatings under Corrosive Conditions

Coating Deterioration and Underlying Metal Corrosion Processes in Water-Line Area: Role of DACs

PROGRESS IN EFFECT OF COATING DEFECTS ON CORROSION BEHAVIOR OF METAL SUBSTRATE BENEATH CONTINGS

Research Progress of Marine Anti-corrosion and Wear-resistant Coating

Modification, Degradation and Evaluation of a Few Organic Coatings for Some Marine Applications

Preparation and Corrosion Performance of Electrophoretic Epoxy Coatings Doped with ZrO2

Degradation Damage of Stress Corrosion in Epoxy Zinc-Rich Coating/Steel Substrate Systems

Corrosion resistances of metallic materials in environments containing chloride ions: A review

Progress in corrosion problem in process of supercritical water oxidation

Synergistic effects of fluid flow and hydrostatic pressure on the degradation of epoxy coating in the simulated deep-sea environment

A Comprehensive Review on Smart Anti-Corrosive Coatings

The corrosion deterioration of reinforced passivation Film: The impact of defects

Comparative Studies on the Deterioration Process of Organic Coatings under Immersed and Cyclic Wet-Dry Conditions by EIS

Corrosion Behavior and Mechanism of WC-12Co Coating in Salt Spray Environment

From Wet to Protective: Film Formation in Waterborne Coatings

The Study Development of Corrosion in Molten Zinc Bath

Degradation Behavior of Arc-Sprayed Zinc Aluminum Alloy Coatings for the Vessel Yongle in the South China Sea

Effect of Chromate on the Electrochemical Behavior of Sintered Zn–Al Coating in Seawater

Development of Novel Environment-friendly Antifouling Materials

Experimental study and finite element analysis of degradation behavior of epoxy zinc-rich coating system under stress corrosion