Multifractal, structural, and optical properties of Mn-doped ZnO films

Chunyu Ma,Wenjuan Wang,Shulin Li,Chunyu Miao,Qingyu Zhang
DOI: https://doi.org/10.1016/j.apsusc.2012.07.150
IF: 6.7
2012-01-01
Applied Surface Science
Abstract:Zn 1-xMn xO (x ≈ 0.07) films were sputter deposited on Si (0 0 1) and fused SiO 2 substrates and were annealed at different temperatures ranging from 600 to 800 °C. The influence of postgrowth annealing on multifractal, structural and optical properties of Zn 1-xMn xO films has been investigated by atomic force microscope (AFM), high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), UV/vis spectrophotometry. A statistical analysis based on multifractal formalism show the nonuniformity of the height distribution increases as the annealing temperature is increased. All as grown and annealed films are textured having preferred orientation along the wurzite c axis. The HRTEM and SAED studies indicate that the Mn doped ZnO film is of high quality, uniform, and free of clustering/segregated phases. The as grown film is in a state of compressive stress and the stress can be largely relieved with annealing temperature of above 700 °C. The optical band gap was found to be 3.25 eV for undoped ZnO film and 3.12 eV for as grown Zn 1-xMn xO (x ≈ 0.07) film. For annealed ZnMnO films the band gap was found to increase continuously with an increase in annealing temperature. © 2012 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?