Abstract:In this present article, we reported a facile and efficient milling method to prepare a series of CuO/PbO nanocomposite metal oxides (CuO/PbO NMOs), with CuO/PbO molar ratios of 1:2, 1:1, 1:0.5, and 1:0.25 as a potential catalyst to catalyze the thermal decomposition of ammonium perchlorate (AP). The obtained CuO/PbO NMOs were systematically characterized. X-ray diffraction (XRD), X-ray energy-dispersive spectrometry (EDS) and X-ray photoelectron spectroscopy (XPS) analyses showed that the characteristic peaks of CuO/PbO NMOs were almost the superposition of nano CuO and nano PbO, while few new weak peaks were observed resulting from the lattice defects and new structural arrangements and chemical bonds between nano CuO and nano PbO during a high-energy grinding process. Scanning electron microscopy (SEM) and transition electron microscopy (TEM) observations exhibited that the particle sizes of the CuO/PbO NMOs were distributed in the range of 10–20 nm. Thermogravimetric (TG) analysis coupled with differential scanning calorimetric (DSC) techniques verified that CuO/PbO NMOs with a CuO/PbO molar ratio of 1:1 presented the best catalytic effect for AP thermal decomposition among the other CuO/PbO NMOs, as well as the single nano CuO and nano PbO. The outstanding catalytic performance is mainly reflected as follows: shifting the peak temperature of AP in high-temperature decomposition stages from 441.3 to 347.6 °C, increasing the decomposition heat of AP from 941 to 1711 J/g, and decreasing the Gibbs free energy of AP from 199.8 to 172.1 kJ/mol, supporting the existence of a synergistic catalytic effect between nano CuO and nano PbO.This article has not yet been cited by other publications.

Shape-Controlled Synthesis of Co3o4 Nanostructures Derived from Coordination Polymer Precursors and Their Application to the Thermal Decomposition of Ammonium Perchlorate

Controlled Synthesis of Co3o4 Single-Crystalline Nanofilms Enclosed by (111) Facets and Their Exceptional Activity for the Catalytic Decomposition of Ammonium Perchlorate

Synthesis of NiO Nanostructures and Their Catalytic Activity in the Thermal Decomposition of Ammonium Perchlorate

Shape-controlled Synthesis of Cobalt Particles by a Surfactant-Free Solvothermal Method and Their Catalytic Application to the Thermal Decomposition of Ammonium Perchlorate

Synthesis and Their Physicochemical Behaviors of Flower-Like Co3O4 Microspheres

Preparation of Coaxial-Line and Hollow Mn2O3 Nanofibers by Single-Nozzle Electrospinning and Their Catalytic Performances for Thermal Decomposition of Ammonium Perchlorate.

A facile route to controlled synthesis of Co<sub>3</sub>O<sub>4</sub> nanoparticles and their environmental catalytic properties

Controllable Synthesis of Co3O4 Octahedra with the Assistance of C2 O2-4

CuO/PbO Nanocomposite: Preparation and Catalysis for Ammonium Perchlorate Thermal Decomposition

Shape-controlled Synthesis and Photocatalytic Activity of in 2 O 3 Nanostructures Derived from Coordination Polymer Precursors

Core-shell structured AP/Fe3O4 composite with enhanced catalytic thermal decomposition property: Fabrication and mechanism study

Preparation of Zn-Co Bimetallic Catalysts and Their Catalytic Properties for Thermal Decomposition of Ammonium Perchlorate

Shape Control of Cobalt Carbonate Particles by a Hydrothermal Process in a Mixed Solvent: an Efficient Precursor to Nanoporous Cobalt Oxide Architectures and Their Sensing Property

Direct Thermal Decomposition of Metal Nitrates in Octadecylamine to Metal Oxide Nanocrystals.

Facile Template Free Shape Controlled Synthesis of α-Fe2O3 Truncated Octahedral Microstructures for the Thermal Decomposition of Ammonium Perchlorate

Controllable hydrothermal-assisted synthesis of mesoporous Co3O4 nanosheets

In situ synthesis of oxidized MXene-based metal cobalt spinel nanocomposites for an excellent promotion in thermal decomposition of ammonium perchlorate

The Synthesis of Ultra-Long Cobalt Chains and Its Outstanding Catalytic Performance on the Thermal Decomposition of Ammonium Perchlorate

Shape control of CoO and LiCoO<sub>2</sub> nanocrystals

Morphology-controlled synthesis of Co 3 O 4 by one step template-free hydrothermal method

Shape control of CoO and LiCoO 2 nanocrystals