Abstract:In this study, Spark Plasma Sintering (SPS) was utilized to fabricate fine-grained cemented carbides, and an orthogonal experimental design was employed to examine the influence of holding temperature (1100 °C, 1200 °C, 1300 °C) and holding time (5, 10, and 15 min) on the performance of WC-10Co cemented carbide specimens. Compared with conventional sintering methods, this work achieved the production of samples with enhanced overall performance at lower temperatures and shorter durations. Specifically, under the conditions of a holding temperature of 1300 °C and a holding time of 5 min, the resulting specimens exhibited a density of 14.64 g/cm3, a hardness of 91.29 HRA, a fracture toughness of 16.39 MPa·m½, and a transverse rupture strength of 2398 MPa. The microstructural analysis revealed that as the holding temperature increased, the Co phase in the specimens underwent a transformation from its initial powder form to banded cobalt and subsequently to slit-shaped cobalt. It was found that the presence of banded cobalt effectively hinders crack propagation, whereas slit-shaped cobalt is more effective in preventing crack initiation, thus impacting the overall performance of the specimens. By analyzing the sintering curves and microstructures, the densification mechanisms during SPS sintering of WC-Co cemented carbides were elucidated. The study concluded that the state changes of the Co phase play a significant role in the densification behavior, final microstructure, and properties of the sintered material. These findings offer valuable insights for understanding and optimizing the SPS process.

Densification and grain growth of microwave sintered WC-Co cemented carbide

Mechanical Properties and Microstructural Behaviour of Microwave Sintered WC–Co

Preparation and mechanical properties of SiCw-reinforced WC-10Ni3Al cemented carbide by microwave sintering

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Fabrication and Properties of Axisymmetric WC/Co Functionally Graded Hard Metal via Microwave Sintering

Investigation of TiC formation during ball-milling of elemental titanium and carbon

L1 2 strengthening of WC-CoNiFe cemented carbides by spark plasma sintering

Densification and grain growth of alumina by microwave processing

Fabrication of Diamond-WC-Based Cemented Carbide Composites by Microwave Sintering

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Role of Co Content on Densification and Microstructure of WC–Co Cemented Carbides Prepared by Selective Laser Melting

Characteristics of 14Cr-ODS ferritic alloy fabricated by mechanically alloying and microwave sintering

Microstructure Evolution in the Cemented Carbides Wc-Coi. Effect of the C/W Ratio on the Morphology and Defects of the Wc Grains

Microstructure and properties of coarse WC-10CoCrFeMnNi cemented carbide by mechanical alloying and hot pressing sintering

Sintering behavior of WC-10Co-V(C, N) nanocrystalline gradient cemented carbide

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC

Effect of carbon content on the microstructure and properties of Cr-doped WC–15Co cemented carbide

Effect of particle size and high-energy ball milling time on microstructure and mechanical properties of WC-10Co cemented carbides with plate-like WC grains

Microstructure and properties of WC-12Co cemented carbide fabricated via selective electron beam melting

PROCESS AND MECHANISM OF MICROWAVE SINTERING OF SiC-Cu/Al COMPOSITES