Growth and Spectral Properties of Yb∶ NdPO4 Crystal

Yong-zheng WANG,Jing LI,Ji-yang WANG,Shu-juan HAN,Yong-jie GUO,Lan-ling ZHAO,Yang ZHANG

2012-01-01

Abstract:Yb:NdPO 4 crystals were grown by a spontaneous nucleation method using Li 2CO 3-2MoO 3 as flux. The as-grown crystals were characterized by X-ray powder diffraction(XRPD) and energy dispersive X-ray spectroscopy(EDS). The results show that the as-grown crystals were well crystallized and some Yb 3+ were doped in the crystals. The transmittance spectra of the as-grown crystal and NdPO 4 crystal were compared. The fluorescence spectrum of as-grown crystal was also measured pumped at 332 nm at room temperature. The strongest fluorescence-emission peak locates at 995 nm, which can be attributed to the 2F 5/2→ 2F 7/2 emission band of Yb 3+. The peak locating at 1059 nm corresponds to the 4F 3/2→ 4I 11/2 emission band of Nd 3+. The results indicate there should be energy transfer from Nd 3+to Yb 3+at room temperature.