Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Shape-controlled synthesis of lead zirconate titanate nanocrystallites, microrods, microrolls and 3D complex architectures via the effects of poly-vinylalcohol macromolecular conformation

Pva Assisted Synthesis of Nanosized Perovskite Pzt Powder by A Two-Stage Precipitation Route

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Shape Evolution Of Pb (Zr,Ti)O-3 Nanocrystals Under Hydrothermal Conditions

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Polymer‐Assisted Hydrothermal Synthesis of Single‐Crystalline Tetragonal Perovskite PbZr0.52Ti0.48O3 Nanowires

Disk-Shaped Colloids: the Synthesis and Applications of ZrP Crystals

Synthesis and Exfoliation of Discotic Zirconium Phosphates to Obtain Colloidal Liquid Crystals

Phase Formation and Free Agglomeration of the PZT Perovskite Powders Prepared via Precipitation Route: Effects of PVA

Synthesis and Characterization of Mesoporous SrTiO3 Spheres Via a Poly Vinyl Alcohol‐Assisted Hydrothermal Route

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Effect of KOH Concentration on the Phase and Morphology of Hydrothermally Synthesized Pb0.70La0.30TiO3 Fine Powders

Hydrothermal Synthesis and Characterization of Single-Crystal Lead Titanate Nanoflakes

Highly Oriented Growth of PbTiO3 Ferroelectric Nanostructure Directed by Organic Molecules under Hydrothermal Condition

Hydrothermal Synthesis of Single-Crystalline Perovskite PbTiO3 Nanosheets with Dominant (001) Facets

Hydrothermal synthesis and characterization of lead titanate perovskite tetragonal microplates

Hydrothermal Synthesis and Morphology Evolution of Perovskite PbTiO<sub>3</sub> Crystals with Different Lead Sources

Synthesis and Thermal Stability of Perovskite PbZr0.52Ti0.48O3 (PZT) Powders Via Precipitation Routes

Hydrothermal Synthesis and Photoluminescence of Pre-Perovskite Lead Titanate Nanofibers