Abstract:A novel ligand-assisted assembly approach is demonstrated for the synthesis of thermally stable and large-pore ordered mesoporous titanium dioxide with a highly crystalline framework by using diblock copolymer poly(ethylene oxide)-b-polystyrene (PEO-b-PS) as a template and titanium isopropoxide (TIPO) as a precursor. Small-angle X-ray scattering, X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution scanning electron microscopy, and N-2-sorption measurements indicate that the obtained TiO2 materials possess an ordered primary cubic mesostructure with large, uniform pore diameters of about 16.0 nm, and high Brunauer-Emmett-Teller surface areas of -112 m(2) g(-1), as well as high thermal stability (similar to 700 degrees C). High resolution TEM and wide-angle XRD measurements clearly illustrate the high crystallinity of the mesoporous titania with an anatase structure in the pore walls. It is worth mentioning that, in this process, in addition to tetrahydrofuran as a solvent, acetylacetone was employed as a coordination agent to avoid rapid hydrolysis of the titanium precursor. Additionally, stepped evaporation and heating processes were adopted to control the condensation rate and facilitate the assembly of the ordered mesostructure, and ensure the formation of fully polycrystalline anatase titania frameworks without collapse of the mesostructure. By employing the obtained mesoporous and crystallized TiO2 as the photoanode in a dye-sensitized solar cell, a high power-conversion efficiency (5.45%) can be achieved in combination with the N719 dye, which shows that this mesoprous titania is a great potential candidate as a catalyst support for photonic-conversion applications.

Formation of Grid-Like Mesoporous Titania Film Via Structural Transformation and Its Surface Superhydrophilicity Conversion

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Natural Hydrophobicity and Reversible Wettability Conversion of Flat Anatase TiO₂ Thin Film.

Effect of Surface Morphology on Wettability Conversion

Synthesis of porous titania thin films using carbonatation reaction and its hydrophilic property

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Sandwich-like titania thin films with one/three-dimensional nanostructures for photocatalytic applications

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

Thermal Stability and Optimal Photoinduced Hydrophilicity of Mesoporous Tio2 Thin Films

Supercritical Fluid Processing of Thermally Stable Mesoporous Titania Thin Films with Enhanced Photocatalytic Activity

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Fabrication Of Macroporous Titanium Dioxide Film Using Pmma Microspheres As Template

Effect of surface microstructure on the photoinduced hydrophilicity of porous TiO2 thin films

Substrate-Assisted Crystallization and Photocatalytic Properties of Mesoporous Tio2 Thin Films

Porous titania surfaces on titanium with hierarchical macro- and mesoporosities for enhancing cell adhesion, proliferation and mineralization.

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Synthesis and Characterization of Hierarchical Titania-Silica Monolith

Ligand‐Assisted Assembly Approach to Synthesize Large‐Pore Ordered Mesoporous Titania with Thermally Stable and Crystalline Framework

Hydrophilic Titania Thin Films from a Molecular Precursor Film Formed via Electrospray Deposition on a Quartz Glass Substrate Precoated with Carbon Nanotubes

Synthesis and Characterization of Mesoporous TiO2 with Wormhole-Like Framework Structure