Hydrophilic Titania Thin Films from a Molecular Precursor Film Formed via Electrospray Deposition on a Quartz Glass Substrate Precoated with Carbon Nanotubes
Natangue Heita Shafudah,Hiroki Nagai,Yutaka Suwazono,Ryuhei Ozawa,Yukihiro Kudoh,Taiju Takahashi,Takeyoshi Onuma,Mitsunobu Sato
DOI: https://doi.org/10.3390/coatings10111050
IF: 3.236
2020-10-29
Coatings
Abstract:Titania precursor films were electrosprayed on a quartz glass substrate, which was pre-modified with an ultra-thin film obtained by spin-coating a single-walled carbon nanotube (SWCNT) dispersed solution. The X-ray diffraction patterns of the thin films obtained by heat-treating the precursor films at 500 °C in air for 1 h indicated that the formed crystals were anatase. A new route to fabricate transparent thin films on the insulating substrate via electrospray deposition (ESD) was thus attained. The photoluminescence spectrum of the thin film showed a peak at 2.23 eV, assignable to the self-trapped exciton of anatase. The Raman spectrum of the thin film demonstrated that heat treatment is useful for removing SWCNTs. The thin film showed a water contact angle of 14 ± 2° even after being kept under dark conditions for 1 h, indicating a high level of hydrophilicity. Additionally, the thin film had a super-hydrophilic surface with a water contact angle of 1 ± 1° after ultraviolet light irradiation with an intensity of 4.5 mW cm−2 at 365 nm for 1 h. The importance of Ti3+ ions in the co-present amorphous phase, which was dominantly formed via the ESD process, for hydrophilicity was also clarified by means of X-ray photoelectron spectroscopy.
materials science, multidisciplinary,physics, applied, coatings & films