Abstract:This article reports on the fabrication of hybrid silica nanoparticles densely grafted with thermoresponsive poly(N-isopropylacrylamide) (PNIPAM) brushes and their thermal phase transition behavior. Surface-initiated atom transfer radical polymerization (ATRP) of N-isopropylacrylamide (NIPAM) was conducted in 2-propanol at ambient temperature using CuCl/CUCl2/tris(2-(dimethylamino)ethyl)amine (Me6TREN) as the catalytic system, starting from the surface of silica nanoparticles derivatized with ATRP initiators (0.35 nm(2)/initiator). The surface-initiated ATRP can be conducted in a well-controlled manner, as revealed by the linear kinetic plot, linear evolution of number-average molecular weights (M-n) versus monomer conversions, and the relatively narrow molecular weight distributions (M-w/M-n < 1.25) of the grafted PNIPAM chains. The grafting density of PNIPAM chains, at the surface of silica nanoparticls was estimated to be 2.2 nm(2)/chain based on transmission electron microscopy (TEM) and thermogravimetric analysis (TGA) characterization results. Laser light scattering (LLS) and optical transmittance were then employed to study the thermal phase transitions of PNIPAM brushes at the surface of silica nanoparticles. Both the intensity-average hydrodynamic radius, < R-h >, and average radius of gyration, < R-h >, exhibit a two-stage decrease upon heating over the broad temperature range of 20-37 degrees C, which is in contrast to the fact that free PNIPAM homopolymer in aqueous solution exhibits a phase transition at ca. 32 degrees C within a narrow temperature range. The first phase transition takes place in the temperature range of 20-30 degrees C, which can be tentatively ascribed to the n-cluster-induced collapse of the inner region of PNIPAM brushes close to the silica core; the second phase transition occurs above 30 degrees C, which can be ascribed to the outer region of PNIPAM brushes, possessing much lower chain density compared to that of the inner part. We tentatively expect that the observed unique double phase transition behavior of polymer brushes coated at the surface of inorganic nanoparticle cores can be further utilized to fabricate novel narrostructured devices with more complex functions.

Preparation of Thermosensitive Pnipam Microcontainers and A Versatile Method to Fabricate Pnipam Shell on Particles with Silica Surface

Antiplatelet and Thermally Responsive Poly(N-Isopropylacrylamide) Surface with Nanoscale Topography

Preparation of wormlike PNIPAM microcontainers with magnetic nanoparticle inclusions

Preparation of P(NIPAM-co-AA) Microcontainers Surface-Anchored with Magnetic Nanoparticles.

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

Preparation of thermoresponsive core–shell polymeric microspheres and hollow PNIPAM microgels

Thermoresponsive Self-Assembled Nipam-Zwitterion Copolymers

Thermosensitive ZrP-PNIPAM Pickering Emulsifier and the Controlled-Release Behavior.

Organic‐Dye‐Coupled Magnetic Nanoparticles Encaged Inside Thermoresponsive PNIPAM Microcapsules

Preparation of Thermo-Sensitive Core-Shell Polymeric Nanospheres Via "in Situ" Polymerization Method

Preparation and Characterization of Thermosensitive Organic–inorganic Hybrid Microgels with Functional Fe3O4 Nanoparticles As Crosslinker

Microfluidic preparation of monodisperse polymeric microspheres coated with silica nanoparticles

Thermoresponsive hollow polymeric shell nano/microparticles with interconnected nanoholes

Biomimic preparation of highly dispersible silica nanoparticles based polymer nanocomposites

Study of the Core−Shell Nanoparticle Formed Through the “Coil-to-globule” Transition of Poly(N-isopropylacrylamide) Grafted with Poly(ethylene Oxide)

Preparation Of Monodisperse Silica/Pmma Core/Shell Nanoparticles With Controllable Shell Thickness By Soap-Free Emulsion Polymerization

P(NIPAm-co-TMSPMA)/Silica Hybrid Microgels: Structures, Swelling Properties and Applications in Fabricating Macroporous Silica

One-step Preparation of Biocompatible Amphiphilic Dimer Nanoparticles with Tunable Particle Morphology and Surface Property for Interface Stabilization and Drug Delivery

Adjustment of responsive temperature and loading behavior of temperature-sensitive core-shell micelles prepared via in-situ polymerization

Fabrication of Hybrid Silica Nanoparticles Densely Grafted with Thermoresponsive Poly(N-isopropylacrylamide) Brushes of Controlled Thickness Via Surface-Initiated Atom Transfer Radical Polymerization

Preparation and Characterization of Multiresponsive Polymer Composite Microspheres with Core–shell Structure