Abstract:This article reports on the fabrication of hybrid silica nanoparticles densely grafted with thermoresponsive poly(N-isopropylacrylamide) (PNIPAM) brushes and their thermal phase transition behavior. Surface-initiated atom transfer radical polymerization (ATRP) of N-isopropylacrylamide (NIPAM) was conducted in 2-propanol at ambient temperature using CuCl/CUCl2/tris(2-(dimethylamino)ethyl)amine (Me6TREN) as the catalytic system, starting from the surface of silica nanoparticles derivatized with ATRP initiators (0.35 nm(2)/initiator). The surface-initiated ATRP can be conducted in a well-controlled manner, as revealed by the linear kinetic plot, linear evolution of number-average molecular weights (M-n) versus monomer conversions, and the relatively narrow molecular weight distributions (M-w/M-n < 1.25) of the grafted PNIPAM chains. The grafting density of PNIPAM chains, at the surface of silica nanoparticls was estimated to be 2.2 nm(2)/chain based on transmission electron microscopy (TEM) and thermogravimetric analysis (TGA) characterization results. Laser light scattering (LLS) and optical transmittance were then employed to study the thermal phase transitions of PNIPAM brushes at the surface of silica nanoparticles. Both the intensity-average hydrodynamic radius, < R-h >, and average radius of gyration, < R-h >, exhibit a two-stage decrease upon heating over the broad temperature range of 20-37 degrees C, which is in contrast to the fact that free PNIPAM homopolymer in aqueous solution exhibits a phase transition at ca. 32 degrees C within a narrow temperature range. The first phase transition takes place in the temperature range of 20-30 degrees C, which can be tentatively ascribed to the n-cluster-induced collapse of the inner region of PNIPAM brushes close to the silica core; the second phase transition occurs above 30 degrees C, which can be ascribed to the outer region of PNIPAM brushes, possessing much lower chain density compared to that of the inner part. We tentatively expect that the observed unique double phase transition behavior of polymer brushes coated at the surface of inorganic nanoparticle cores can be further utilized to fabricate novel narrostructured devices with more complex functions.

Fabrication of Hybrid Silica Nanoparticles Densely Grafted with Thermoresponsive Poly(N-isopropylacrylamide) Brushes of Controlled Thickness Via Surface-Initiated Atom Transfer Radical Polymerization

Antiplatelet and Thermally Responsive Poly(N-Isopropylacrylamide) Surface with Nanoscale Topography

Controlled Grafting of Well-Defined Polymers on Hydrogen-Terminated Silicon Substrates by Surface-Initiated Atom Transfer Radical Polymerization

Composite silica nanospheres covalently anchored with gold nanoparticles at the outer periphery of thermoresponsive polymer brushes

Fabrication Of Thermoresponsive Cross-Linked Poly(N-Isopropylacrylamide) Nanocapsules And Silver Nanoparticle-Embedded Hybrid Capsules With Controlled Shell Thickness

One-step grafting reaction of thermoresponsive polymer brushes over silica nanoparticles

Preparation of Poly(N-Isopropylacrylamide) Brush Grafted Silica Particles Via Surface-Initiated Atom Transfer Radical Polymerization Used for Aqueous Chromatography

Synthesis of Thermoresponsive Silica Nanoparticle/Pnipam Hybrids by Aqueous Surface-Initiated Atom Transfer Radical Polymerization

Synthesis and Characterization of Silica Nanoparticles with Well-Defined Thermoresponsive PNIPAM Via a Combination of RAFT and Click Chemistry.

Thermoresponsive Amphiphilic Janus Silica Nanoparticles Via Combining “polymer Single-Crystal Templating” and “Grafting-From” Methods

Fabrication of Hybrid Nanoparticles with Thermoresponsive Coronas Via A Self-Assembling Approach

Preparation of Polysulfone-G-Poly(N-Isopropylacrylamide) Graft Copolymers Through Atom Transfer Radical Polymerization and Formation of Temperature-Responsive Nanoparticles

Fabrication and Phase Behavior of Thermo- And/or Ph-Responsive Polymer-Grafted SiO2 Nanoparticles

Synthesis and Characterization of Gibbsite Nanoplatelet Brushes by Surface-Initiated Atom Transfer Radical Polymerization

Poly(<i>N</i>-isopropylacrylamide) Brush Fabricated by Surface-Initiated Photopolymerization and its Response to Temperature

Synthesis and Characterization of Poly(γ‐methacryloxypropyltrimethoxysilane)‐grafted Silica Hybrid Nanoparticles Prepared by Surface‐initiated Atom Transfer Radical Polymerization

Synthesis of Hydrophobic Polymer Brushes on Silica Nanoparticles Via the Combination of Surface-Initiated ATRP, ROP and Click Chemistry

Synthesis and Phase Transition of Poly(N-isopropylacrylamide)-Based Thermo-Sensitive Cyclic Brush Polymer.

Fabrication of Photoswitchable and Thermotunable Multicolor Fluorescent Hybrid Silica Nanoparticles Coated with Dye-Labeled Poly(N-Isopropylacrylamide) Brushes

Functionalized Si3N4 nanoparticles modified with hydrophobic polymer chains by surface-initiated atom transfer radical polymerization (ATRP)

Synthesis of SiO_2/PNIPAm Hybrid Microspheres by Combination of RAFT and Thiol-ene Click Chemistry