Novel hierarchically ordered porous vanado-silicate nanocomposites for the application in industrial catalysis

Matthew Howard,Jacob Whittle,Fan Zhang,Dongyuan Zhao,Tapas Sen
2012-01-01
Abstract:Hierarchically ordered porous vanado-silicate (HOPVS) nanocomposties were prepared by multiple templating route such as polystyrene latex spheres, tri-block copolymer F-127 (E0(107)PO(70)EO(107)) in the presence of a co-solvent (n-butanol). Novel materials exhibited high surface area consisting of macropores of diameter similar to 330nm with interconnecting windows of similar to 80nm. The walls of the macropores were formed with disordered meso (similar to 7 nm diameter) and microporosity (< 2 nm diameter). Vanadyl (VO4+) species were homogeneously dispersed in the uncalcined nanocomposites (8 line hyperfine patterns in V-51 EPR signal) whereas calcined form exhibited no hyperfine pattern due to the aerial oxidation of paramagnetic (VO4+) species to diamagnetic vanadium species. The calcined form exhibited good catalytic activity for the (i) oxidation of toluene to benzaldehyde, benzyl alcohol and cresols; (ii) oxidation of cis-cyclooctene to cyclooctene oxide; (iii) oxidation of phenanthrene to biphenyl 2,2-dicarbaldehyde and 9,10 phenantrhaquinone in the presence of hydrogen peroxide.
What problem does this paper attempt to address?