Abstract:Continuous carbon fiber reinforced silicon carbide matrix composites (C/SiCs) have been widely used in aeronautic and astronautic fields because of their more attractive high temperature properties with less structural weight. However, density defects (DD) with randomness and unpredictability will have a serious impact on the mechanical properties of the laminated C/SiC composites (2D C/SiCs). A novel method was presented, by masking graphite-papers with different sizes on the surface of the ground C/SiC composite plates and then automatically produced various size low density region to tentatively imitate the DD once high temperature fabrication of SiC matrix. The mechanical reduction on 2D C/SiCs with different size DD (R-dd, thus was defined as ratio of DD width D to whole sample length L) was investigated subsequently. Results show that, tensile strength of the C/SiCs continuously decreased from original 241.7 MPa to final 212.2 MPa when the R-dd below 30%. There trended to stable tendency above 88.8% of original strength with further increase of the R-dd. Meanwhile, compressive strength was subjected to a larger decrease from original 280.3 MPa to final 232.2 MPa and then tended to be constant at 82.2% of original strength when the R-dd further increased. The compressive strength decreased to a greater extent and tended to stabilize earlier as the R-dd increased. It pointed out that the DD caused higher sensitivity to the compressive strength of the C/SiCs than to the tensile strength. In addition, as the R-dd increased, both tensile and compressive elastic modulus decreased to the nearly same extent, eventually falling to 83.25% of the initial value, indicating that the increased DD fewly further reduced the stiffness.

Nondestructive investigation of density defect in C/SiCs and its effect on the mechanical properties

Designable Density Defect Influencing the Mechanical Property of 3D Needled C/SiC Composites

Study on the influence of manufacturing defects on coefficient of thermal expansion of plain weave C/SiC

Pore Evolution and Mechanical Response under Locally Varying Density Defects in Ceramic Matrix Composites

Nondestructive testing and evaluation of 2D C/SiC with defects

Non-destructive Testing and Evaluation of 3D Needled C/SiC Plate with Density Gradient

Controlled Deposition of Density Defects for Understanding Mechanical Reduction on 2D C/SiC Composites

Infrared thermal wave imaging for nondestructive detection and measurement of the C/SiC composites

Nondestructive Testing Of Defect In A C/Sic Composite

Nondestructive Evaluation and Mechanical Characterization of a Defect‐Embedded Ceramic Matrix Composite Laminate

Infrared Thermography For Non-Destructive Evaluation Of 2d C/Sic Composites Under Fatigue Loading

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Non-destructive Investigation of Quasi-Static Indentation Damage to C/SiC Composites and Its Effects on Compressive Properties

Microstructure and Compressive Behaviour of 3D Needled C/SiC Composites

Effect of a Diffusion-Enhancing Hole on the Densification of a Thick-Section 2D C/SiC Composite

3D Characterizations of Pores and Damages in C/SiC Composites by Using X-Ray Computed Tomography

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THREE-DIMENSIONAL NEEDLED C/SiC COMPOSITE

Internal Damage Evolution Investigation of C/SiC Composites Using In-Situ Tensile X-ray Computed Tomography Testing and Digital Volume Correlation at 1000 °C

Effects of Void Defects on Fracture Features and Tensile Strength of C/SiC Composites: an Image-based FEM Study

Microstructure and mechanical properties of 3D needled carbon fibre reinforced carbon and silicon carbide composites

The study of inspection on SiC coated carbon-carbon composite with subsurface defects by lock-in thermography