Abstract:AlH3 is a metastable hydride with a theoretical hydrogen capacity of 10.01 wt % and is very easy to decompose during ball milling especially in the presence of many catalysts, which will lead to the attenuation of the available hydrogen capacity. In this work, AlH3 was ball milled in air (called "air-milling") with layered Ti3C2 to prepare a Ti3C2-catalyzed AlH3 hydrogen storage material. Such air-milled and Ti3C2-catalyzed AlH3 possesses excellent hydrogen storage performances, with a low initial decomposition temperature of just 61 °C and a high hydrogen release capacity of 8.1 wt %. In addition, 6.9 wt % of hydrogen can be released within 20 min at constantly 100 °C, with a low activation energy as low as 40 kJ mol-1. Air-milling will lead to the formation of an Al2O3 oxide layer on the AlH3 particles, which will prevent continuous decomposition of AlH3 when milling with active layered Ti3C2. The layered Ti3C2 will grip on and intrude into the AlH3 particle oxide layers and then catalyze the decomposition of AlH3 during heating. The strategy employing air-milling as a synthesis method and utilizing layered Ti3C2 as a catalyst in this work can solve the key issue of severe decomposition during ball milling with catalysts economically and conveniently and thus achieve both high-capacity and low-temperature hydrogen storage of AlH3. This air-milling method is also effective for other active catalysts toward both reducing the decomposition temperature and increasing the available hydrogen capacity of AlH3.

Enhancing Hydrogen‐Generation Performance of Γ‐al2o3 Modified Al Powder by Ultrasonic Dispersion

A Novel Approach for Enhancing Hydrogen Production from Bio-Glycerol Photoreforming by Improving Colloidal Dispersion Stability.

Improved Hydrogen Generation from the Hydrolysis of Aluminum Ball Milled with Hydride

Study on Hydrogen Generation from the Hydrolysis of a Ball Milled Aluminum/calcium Hydride Composite

Hydrogen generation from the hydrolysis of Mg powder ball-milled with AlCl3

Design and Fabrication of High Activity Retention Al-Based Composite Powders for Mild Hydrogen Generation

Synergistic effect and mechanisms of ultrasound and AlOOH suspension on Al hydrolysis for hydrogen production

Enhanced Hydrogen Generation Performance of Al-Rich Alloys by a Melting-Mechanical Crushing-Ball Milling Method

Enhanced hydrogen generation from Al-water reaction mediated by metal salts

Effect of Salts Addition on the Hydrogen Generation of Al–LiH Composite Elaborated by Ball Milling

Hydrogen Generation from the Reaction of Al-based Composites Activated by Low-Melting-point Metals/oxides/salts with Water

Investigation on the Improved Hydrolysis of Aluminum–calcium Hydride-Salt Mixture Elaborated by Ball Milling

Hydrogen Production from Aluminum-Water Reactions at Low Temperatures: Based on an In-Situ Two Powders of Different Particle Sizes

Mild hydrogen production from the hydrolysis of Al–Bi–Zn composite powder

Experimental Study on the Effect of Low Melting Point Metal Additives on Hydrogen Production in the Aluminum–water Reaction

Dehydriding properties of γ-AlH3

Directed Stabilization by Air-Milling and Catalyzed Decomposition by Layered Titanium Carbide Toward Low-Temperature and High-Capacity Hydrogen Storage of Aluminum Hydride

Hydrogen generation from Al‐water reaction catalyzed by Fe/AlOOH composite

Enhanced hydrogen production from Al-water reaction: Strategies, performances, mechanisms and applications

A Novel AlGa@Gr Material for Ultrasound Enhanced Hydrogen Generation

Metal Substrate Enhanced Hydrogen Production of Aluminum Fed Liquid Phase Ga–In Alloy Inside Aqueous Solution