Abstract:In this study, we develop an efficient approach to fabricate superhydrophobic aluminum alloy samples. The superhydrophobic aluminum alloy sample is prepared by combining high-speed wire electrical discharge machining, a short-time chemical etching method, with a modification treatment. The prepared superhydrophobic aluminum sample possesses a contact angle of 158.6 ± 1.3° and a sliding angle of below 1°. The introduction of chemical etching can shorten the preparation time from 20 to 8 h. The prepared superhydrophobic aluminum alloy sample is durable enough to endure the harsh conditions to which some aluminum alloy parts are subjected. Its excellent anti-icing ability is confirmed by the freezing delay test and low-temperature durability test under overcooled conditions. In addition, the prepared superhydrophobic aluminum alloy sample shows superior thermostability and high-temperature durability in the range of 180∼240 °C. Moreover, the prepared superhydrophobic aluminum alloy sample exhibits outstanding mechanical durability that can endure abrasion by 1000-grit sandpaper at 20 kPa for 260 cm. It also can withstand 11 vertical impacts by 200 g weight dropped from 12 cm with the weight falling on the sample at a rate of ∼15.50 cm/s. The introduction of the chemical etching greatly shortens the preparation time and the as-prepared superhydrophobic aluminum alloy sample exhibited excellent durability, which may widen the application range of superhydrophobic aluminum alloys.

Facile fabrication of superhydrophobic nanostructures on aluminum foils with controlled-condensation and delayed-icing effects

Fabrication of Modifier-Free Superhydrophobic Surfaces with Anti-Icing and Self-Cleaning Properties on Ti Substrate by Anodization Method

Optimal conditions for the fabrication of alumina superhydrophobic surfaces via anodization, and its self-cleaning, anti-icing, and cold-resistance capabilities

Fabrication of a Highly Stable Superhydrophobic Surface with Dual-Scale Structure and Its Antifrosting Properties

Fabrication and Characterization of Superhydrophobic Surfaces on Aluminum Alloy Substrates

A Superhydrophobic Self‐Cleaning and Anti‐Icing Aluminum Sheet Fabricated by Alkaline Solution

A simple strategy towards construction of fluorine-free superhydrophobic aluminum alloy surfaces: self-cleaning, anti-corrosion and anti-frost

Superamphiphobic triple-scale micro-/nanostructured aluminum surfaces with self-cleaning and anti-icing properties

Robust superhydrophobic aluminum alloy surfaces with anti-icing ability, thermostability, and mechanical durability

Robust superhydrophobic film on aluminum alloy prepared with TiO 2 /SiO 2 -silane composite film for efficient self-cleaning, anti-corrosion and anti-icing

A Facile Cost-Effective Method for Preparing Superhydrophobic Self-Cleaning Silica Nanoparticles Coating on Al Substrate

Fabrication of Superhydrophobic Surface with Different Metal Films on Aluminum Alloy

Integration of database systems using an object-oriented approach

Robust superhydrophobic surface on Al substrate with durability, corrosion resistance and ice-phobicity

Fabrication of a micro-nanostructured superhydrophobic aluminum surface with excellent corrosion resistance and anti-icing performance

Preparation and anti-frosting performance of super-hydrophobic surface based on copper foil

Robust and Chemically Stable Superhydrophobic Aluminum-Alloy Surface with Enhanced Corrosion-Resistance Properties

Facile Preparation of Hydrophobic Aluminum Oxide Film via Sol-Gel Method

Superhydrophobic Modification of Atomic Layer Deposition Antireflection Aluminum Oxide Film: A Simple Evaporative Coating Technique

A simple fabrication method for mechanically robust superhydrophobic surface by hierarchical aluminum hydroxide structures