Mechanical Control of Surface Adsorption by Nanoscale Cracking.
Qiang Zhuang,Scott C Warren,Bilge Baytekin,Ahmet F Demirörs,Pramod P Pillai,Bartlomiej Kowalczyk,H Tarik Baytekin,Bartosz Grzybowski
DOI: https://doi.org/10.1002/adma.201306335
2014-01-01
Abstract:DOI: 10.1002/adma.201306335 between adjacent cracks must be tunable. Top-down, serial approaches [ 14 ] for initiating cracks provide a simple way to control crack spacing, but even in these cases the crack width typically varies by more than an order of magnitude. Similar variability was observed when thin coatings were cracked using uniaxial strain. [ 26–28 ] Fourth, the crack should not only allow a material to deposit but also impart some degree of selectivity. Ideally, the crack should control the size, shape, and crystallographic orientation of the material that deposits. Fifth, the production of cracks in only specifi c locations of a material would be desirable. Although top-down strategies for initiating cracks one-by-one has been presented, [ 14,15 ] for many materials and applications it would be desirable to identify principles that allow the high throughput production of cracks in a spatially controlled manner. In the present work, we fabricated a composite material that is comprised of a stretchable, [ 29–31 ] polymeric substrate covered with a reactive/charged polymer onto which a monolayer of nanoparticles is adsorbed ( Figure 1 ). The nanoparticle monolayer acts like a mask and, when stretched, fragments controllably as the large, macroscopic deformation divides into the small, nanoscopic movements of adjacent particles. Because the nanoparticles are deposited as a monolayer, the process of cracking unmasks the chemically distinct substrate, thereby enabling selective surface design. Unlike in continuous materials, the cracking process is guided by the discrete nature of nanoparticles and is therefore not limited by a material’s inherent faceting and fracture characteristics. [ 14 ]