Abstract:Production of fibers from nonthermoplastic polymers, such as chitosan, usually requires dissolution with subsequent fiber formation, for instance, via coagulation. Good fiber-forming properties enable simultaneous spinning of multiple fibers into a yarn, which is one of the prerequisites for process scalability. Here, we report a multifilament wet-spinning process that eliminates the use of such volatile organic compounds as methanol and acetone, enhances fiber formation, and allows producing continuous well-separated chitosan fibers after drying. This is achieved by (i) solidification of the extruded solution by alkali and sodium acetate in the coagulation bath and (ii) further stabilization of the fibers by adsorbing the anionic surfactant, sodium dodecyl sulfate. The obtained fibers have a circular cross section and smooth surface. We demonstrate that it is possible to increase fiber breaking tenacity and Young's modulus by applying stretching (draw ratios up to 1.77) or by incorporating cellulose nanofibrils (CNFs, up to 4 wt % based on chitosan) in the spinning solutions. However, the limitation of increased viscosity when adding CNF is needed to be overcome for possible higher reinforcement effects. We demonstrate that fiber breaking tenacity, Young's modulus, and elongation at break can be enhanced even further by increasing the spin dope temperature from 22 to 60 °C, with simultaneously increasing the spin dope solid content to keep the same dope viscosity. The fibers with a maximum breaking tenacity of ca. 10 cN/tex at an elongation at break of ca. 7.5% were obtained.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsapm.0c00562?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsapm.0c00562</a>.Chemical structures of CNF and CNC, microscopy images of chitosan solutions and fibers, rheological data, SEM images, and EDS spectra (<a class="ext-link" href="/doi/suppl/10.1021/acsapm.0c00562/suppl_file/ap0c00562_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Preparation of High Strength Chitosan Fibers by Using Ionic Liquid As Spinning Solution

Wet Spinning of Chitosan Fibers: Effect of Sodium Dodecyl Sulfate Adsorption and Enhanced Dope Temperature

Pure Chitosan-Based Fibers Manufactured by a Wet Spinning Lab-Scale Process Using Ionic Liquids

A New Approach for Preparing Chitosan Fibers from a LiOH/urea Solvent System

Pure chitosan multifilament yarns made using a semi‐industrial pilot scale wet‐spinning process with ionic liquids

Spinning Process of Chitosan Fiber with Low Concentration of Formic Acid Solution and its Characteristics

From Spinning Process to Physical Properties

Chitosan-LiOH-urea Aqueous Solution—a Novel Water-Based System for Chitosan Processing

Continuous Pilot‐Scale Wet‐Spinning of Biocompatible Chitin/Chitosan Multifilaments from an Aqueous KOH/Urea Solution

Preparation and Characterization of Poly(ethylene Glycol)-G-chitosan with Water- and Organosolubility

Wet spinning of chitin nanowhiskers: Effects of electrolyte composition in coagulation baths on mechanical properties and nanowhisker orientation

Liquid Crystal Fibers Produced by Using Electrospinning Technique

Electrospinning of Chitosan Nanofibers: the Favorable Effect of Metal Ions

Hydrogel Films Prepared from LiOH/urea Aqueous Solution of Chitosan

Preparation of alginate–chitosan fibers with potential biomedical applications

Preparation and Characterization of N-succinyl-chitosan

High-Strength Chitosan Hydrogels Prepared from Lioh/Urea Solvent System

Dissolution, Materialization and Derivatization of Chitin and Chitosan in Ionic Liquids

Wet spinning of chitosan and the acetylation of chitosan fibers

Chitosan Membranes from Acetic Acid and Imidazolium Ionic Liquids: Effect of Imidazolium Structure on Membrane Properties