Abstract:Production of fibers from nonthermoplastic polymers, such as chitosan, usually requires dissolution with subsequent fiber formation, for instance, via coagulation. Good fiber-forming properties enable simultaneous spinning of multiple fibers into a yarn, which is one of the prerequisites for process scalability. Here, we report a multifilament wet-spinning process that eliminates the use of such volatile organic compounds as methanol and acetone, enhances fiber formation, and allows producing continuous well-separated chitosan fibers after drying. This is achieved by (i) solidification of the extruded solution by alkali and sodium acetate in the coagulation bath and (ii) further stabilization of the fibers by adsorbing the anionic surfactant, sodium dodecyl sulfate. The obtained fibers have a circular cross section and smooth surface. We demonstrate that it is possible to increase fiber breaking tenacity and Young's modulus by applying stretching (draw ratios up to 1.77) or by incorporating cellulose nanofibrils (CNFs, up to 4 wt % based on chitosan) in the spinning solutions. However, the limitation of increased viscosity when adding CNF is needed to be overcome for possible higher reinforcement effects. We demonstrate that fiber breaking tenacity, Young's modulus, and elongation at break can be enhanced even further by increasing the spin dope temperature from 22 to 60 °C, with simultaneously increasing the spin dope solid content to keep the same dope viscosity. The fibers with a maximum breaking tenacity of ca. 10 cN/tex at an elongation at break of ca. 7.5% were obtained.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsapm.0c00562?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsapm.0c00562</a>.Chemical structures of CNF and CNC, microscopy images of chitosan solutions and fibers, rheological data, SEM images, and EDS spectra (<a class="ext-link" href="/doi/suppl/10.1021/acsapm.0c00562/suppl_file/ap0c00562_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Wet spinning of chitosan and the acetylation of chitosan fibers

Spinning Process of Chitosan Fiber with Low Concentration of Formic Acid Solution and its Characteristics

Wet Spinning of Chitosan Fibers: Effect of Sodium Dodecyl Sulfate Adsorption and Enhanced Dope Temperature

Synthesis and Characterization of Chitosan Oligosaccharide-graft-Acrylic Acid Biodegradable Crosslinker

Wet spinning of chitin nanowhiskers: Effects of electrolyte composition in coagulation baths on mechanical properties and nanowhisker orientation

A New Approach for Preparing Chitosan Fibers from a LiOH/urea Solvent System

Effect of Acetylation on the Nanofibril Formation of Chitosan from All-Atom De Novo Self-Assembly Simulations

Pure chitosan multifilament yarns made using a semi‐industrial pilot scale wet‐spinning process with ionic liquids

Pure Chitosan-Based Fibers Manufactured by a Wet Spinning Lab-Scale Process Using Ionic Liquids

Wet spinning of fibers made of chitosan and chitin nanofibrils

Flexible fibers wet-spun from formic acid modified chitosan

Continuous Pilot‐Scale Wet‐Spinning of Biocompatible Chitin/Chitosan Multifilaments from an Aqueous KOH/Urea Solution

Grafting of chitosan-acrylamide hybrid on the wool: Characterization, reactive dyeing, antioxidant and antibacterial studies

Effect of Treatment Methods on Chitin Structure and Its Transformation into Nitrogen‐Containing Chemicals

Effects of graft modification on the properties of chitosan for warp sizing

A review on chitin dissolution as preparation for electrospinning application

Homogeneous Acetylation Of Chitosan In Ionic Liquids

From Spinning Process to Physical Properties

Evaluating the strategies to improve strength and water-resistance of chitin nanofibril assembled structures: Molecule-bridging, heat-treatment and deacidifying

Grafting of Chitosan: Structural, Thermal and Antimicrobial Properties