Abstract:Existing nano-Mo2C preparation methods suffer from expensive raw materials, subtle operation demands and complex synthesis steps. Herein, both theoretical and experimental studies were performed to develop a more efficient and economical method for nano-Mo2C preparation. Reaction thermodynamics of gas-vapor system of CH4-MoO3-N2 indicates that high-proportion inert gas significantly increases the required carbonization potential (CO/CO2) for Mo2C formation, but surplus carbon produced from methane decomposition can trigger water gas producing reaction and Boudouard reaction to help meet the requirement. Nano-Mo2C was then synthesized by mixing N2-carried MoO3 vapor with CH4 under varying conditions including temperature, gas flowrate and vapor concentration. It is found that MoO3 vapor experienced conversions to monoclinic MoO2 to cubic Mo to hexagonal Mo2C, and all these stages could be finished in as short as about 6 s at 1100 °C with initial molar ratio of CH4 to MoO3 over 3.5. The final products were present as porous plate-like single crystals or chain-like polycrystals, which are determined by initial vapor concentration and gas flowrate. Furtherly, electrocatalytic properties of Mo2C nanocrystals for hydrogen evolution reaction were measured, and the sample with the largest specific surface area and cleaner surface showed competitive performance over reported nano-Mo2C.

Synthesis of Superconducting Sphere‐like Mo2C Nanoparticles in an Autoclave

Synthesis of Nanocrystalline Mo{sub 2}C Via Sodium Co-Reduction of MoCl{sub 5} and CBr{sub 4} in Benzene

A Facile Preparation of Nanocrystalline Mo2C from Graphite or Carbon Nanotubes.

Synthesis of Nanocrystalline Mo2C Via Sodium Co-Reduction of MoCl5 and CBr4 in Benzene

Atomic-Scale Mechanism on Nucleation and Growth of Mo2c Nanoparticles Revealed by in Situ Transmission Electron Microscopy

Enhancing the specific capacity and rate performance of MoS<sub>2</sub> nanomaterials <i>via</i> introducing subgrains at a hydrothermal temperature 160 C

A Simple Approach To Synthesize Mo2n Nanocrystals

Solution Phase Synthesis of Superconducting La2CuO4 Microspheres

A Novel Route to Nanosized Molybdenum Boride and Carbide And/Or Metallic Molybdenum by Thermo-Synthesis Method from Moo3, Kbh4, and Ccl4

Thermodynamics guided ultrafast and continuous preparation of Mo2C nanocrystals for hydrogen evolution electrocatalysis

Room Temperature Synthesis of Hollow CdMoO4 Microspheres by a Surfactant-Free Aqueous Solution Route

Synthesis Nano-Sicp/Mosi2 Composites by In-Situ Reaction Sintering and Low Temperature Oxidation Behavior

Synthesis of nanocrystalline molybdenum carbide materials and their characterization

Shape-controlled Synthesis of Nanocubic Co3O4 by Hydrothermal Oxidation Method

Preparation, microstructure, electromagnetic property and microwave absorption property of MoS2 nanopowder by hydrothermal method at various reaction temperatures

General Synthesis and Phase Control of Metal Molybdate Hydrates MMoO4·nH2O (M = Co, Ni, Mn, N = 0, 3/4, 1) Nano/Microcrystals by a Hydrothermal Approach: Magnetic, Photocatalytic, and Electrochemical Properties

Solvothermal synthesis and characterization of cobalt sulfide nanocrystals

Synthesis and Characterization of Superconducting NbC Nanotubes

Synthesis of Porous and Hollow Microspheres of Nanocrystalline Mn2O3

Mechanosynthesis of molybdenum carbides by ball milling at room temperature

Low-Temperature Growth of Ultrathin and Epitaxial Mo2C nanosheets via Vapor-Liquid-Solid Process