Room temperature multiferroic properties and polymorphic phase transition-induced noticeable magnetodielectric anomalies in Fe/Co co-doped (K0.52Na0.48)NbO3 ceramics
Min Zhou,Xiaomei Lu,Lin Liu,Junjun Wang,Dingze Lu,Fengzhen Huang,Jinsong Zhu,Pengfei Cheng,Qiuping Wang
DOI: https://doi.org/10.1016/j.jallcom.2020.155519
IF: 6.2
2020-09-01
Journal of Alloys and Compounds
Abstract:Polycrystalline ceramics of (K0.52Na0.48)Nb1-x (FeCo) x O3 (0 ≤ x ≤ 0.02) are synthesized using solid-state reaction method. Appropriate Fe/Co doping (x = 0.010 and 0.015) not only optimizes room temperature ferroelectricity of KNNFC ceramics, but also effectively introduces room temperature ferromagnetism and large magnetodielectric effects. The Fe2+/3+-O-Co2+/3+ ferromagnetic double exchange is considered the main reason for the enhancement in ferromagnetic. Moreover, magnetic anomalies and noticeable magnetodielectric (MD) peaks are found near the ferroelectric rhombohedral-orthorhombic (R–O) polymorphic phase transition, indicating the presence of spin-lattice coupling in these samples. Meanwhile, the Fe2+-Fe3+, Co2+-Co3+, and/or Fe2+/3+-Co2+/3+ local dipoles that begin to appear near the R–O phase transition temperature can also contribute to the MD effect. When x = 0.015, the MD peak is as large as +12% (0.9 T, 106 Hz, 120 K), and the room temperature MD value reaches −7% (0.9 T, 106 Hz).
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering