Abstract:In this work, we report a unique synthesis of hierarchical zeolite ZSM-5 monoliths using polyurethane foam (PUF) as a rigid scaffold through a simple steam-assisted crystallization (SAC) method. The resultant monolithic ZSM-5 with a well crystalline structure possesses unique tetra-modal porosity (macropore/macropore/mesopore/micropore). The first modes of macroporosity (pore size of similar to 33 mu m) is formed after the removal of the PUF scaffolds. The second set of macropores with a size of 0.2-1.7 mu m originate from the aggregation of ZSM-5 nanocrystals (crystal size of similar to 500 nm) inside the macropores of the PUF scaffolds. The third level of porosity stems from the intracrystalline mesopores (similar to 53 nm) in each ZSM-5 crystal, along with the fourth intrinsic microporosity of zeolites. The mesopores are derived from the voids formed in the initial dry precursors, which are transformed and preserved as intracrystalline mesopores in each zeolite crystal. This type of ZSM-5 monolith possesses a high macroporosity (75.2%) and mechanical stability (1.2 MPa). The total surface area of the monolithic ZSM-5 is similar to 226 m(2) g(-1) and the total pore volume is similar to 0.21 cm(3) g(-1). The ZSM-5 monolith as a structured catalyst for methanol to propylene (MTP) conversion shows excellent catalytic performance with high methanol conversion (above 95%) and propylene selectivity (above 40%) at a high weight hourly space velocity (WHSV, 3.6 h(-1)). Importantly, the diffusion efficiency of catalyst is remarkably improved. After reaction for 5 h, the selectivity of propylene reaches a steady state.

Vapor Assisted “in Situ” Transformation of Mesoporous Carbon–silica Composite for Hierarchically Porous Zeolites

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Direct Observation Of The Mesopores In Zsm-5 Zeolites With Hierarchical Porous Structures By Laser-Hyperpolarized Xe-129 Nmr

High-Surface-Area Zeolitic Silica with Mesoporosity

Enhanced CO2 Adsorption Performance on Hierarchical Porous ZSM-5 Zeolite

Rapid hydrothermal synthesis of hierarchical ZSM-5/beta composite zeolites

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Facile synthesis of hierarchical porous ZSM-5 zeolite with tunable mesostructure and its application in catalytic cracking of LDPE

A high‐resolution solid‐state NMR study on nano‐structured HZSM‐5 zeolite

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

Mesoporogen-Free Synthesis of Hierarchically Structured Zeolites with Variable Si/Al Ratios via a Steam-Assisted Crystallization Process

In-situ synthesis of hierarchical lamellar ZSM-5 zeolite with enhanced MTP catalytic performance by a facile seed-assisted method

Synthesis of a hierarchically macro-/mesoporous zeolite based on a micro-emulsion mechanism

Sub-micron sized hierarchical porous ZSM-5 particles with controllable mesoporous structures by changing the alkalinity in the synthesis using NaOH

Optimization of crystal growth of hierarchical porosity ZSM-5 zeolite based on coal fly ash "waste utilization"Optimierung des Kristallwachstums hierarchischer Porositat ZSM-5-Zeolith auf Basis von Kohlenflugasche Mull-Verwendung"

Synthesis of hierarchical ZSM-5 with ultra-small mesopore structure and its catalytic performance during methanol to hydrocarbons

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

Directly Transforming As-Synthesized MCM-41 to Mesoporous MFI Zeolite

Facile synthesis of mesoporous ZSM-5 aided by sonication and its application for VOCs capture

Hierarchical Zsm-5 Catalyst Synthesized by A Triton X-100 Assisted Hydrothermal Method