Method to improve high-frequency magnetic characteristics of Fe 80Ni20-O alloy films by introducing low-dose oxygen

Haoran Geng,Yousheng Wang,Jing Wang,Zhiqing Li,Sha Nie,Lin Wang,Yonglu Chen,Dongliang Peng,Haili Bai

DOI: https://doi.org/10.1016/j.matlet.2011.09.064

IF: 3

2012-01-01

Materials Letters

Abstract:In this letter, we propose a method to fabricate Fe80Ni20–O film with improved static and high-frequency, magnetic and electrical properties. Fe80Ni20–O alloy films were prepared by direct current magnetron sputtering at room temperature. The results show that the in-plane uniaxial magnetic anisotropy fields can be adjusted in a broad range by solely adding a very low dose of oxygen into Fe80Ni20 alloy films without applying any inducing field on substrates during deposition. By increasing the oxygen flow ratio from 0.75% to 3%, Fe80Ni20–O alloy films could be achieved with an adjustable ferromagnetic resonance frequency fr (from 2.2 to 5.9GHz), a large saturation magnetization 4πMs (from 16.7 to 15.2kG), and a high resistivity ρ (from 56.7 to 108μΩcm).