The Effects of Pre-Oxidation on the Sintering and Mechanical Property of Powder Injection Moulded Sic Material

Zhen Lu,Zhenlong Wang,Kaifeng Zhang,Changrui Wang

DOI: https://doi.org/10.1016/j.matdes.2011.07.025

IF: 9.417

2012-01-01

Materials & Design

Abstract:Usually, injection moulded SiC green parts are debound in inert atmosphere or vacuum, which induces the residual carbon and increases forming cycle and production cost. In this paper, injection moulded SiC with Al2O3 and Y2O3 as sintering assistant was thermal debound in air and Ar, respectively. The paper investigates the effects of pre-oxidation during debinding stage on the sintering and mechanical property of SiC material. During sintering, the oxide SiO2 is in favour of the shrinkage of debound samples at lower temperature. After sintering, the linear shrinkage of sintered samples with pre-oxidation is bigger than the sample without pre-oxidation. Test results by TEM and XRD indicate that SiO2 disappear from the inside of the sintered samples. The loss of SiO2 decreases the content of Al2O3, which affects the formation of YAG (Y3Al5O12). Sintered Sic samples contain alpha-SiC phase and intergranular phase. There is no heterophase between the boundaries of alpha-SiC phase and intergranular phase. The bending and compression strength values of sintered samples with pre-oxidation reach to 537 MPa and 2.89 GPa, respectively. These values approach the strength of sintered samples without pre-oxidation (594 MPa and 3.0 GPa). (C) 2011 Elsevier Ltd. All rights reserved.