Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Compare the Corrosion of 3%cr Steel with X65 Pipeline Steel in Subsea Co2 Top-Of-Line Corrosion Environment

Corrosion Performance Analysis of Tubing Materials with Different Cr Contents in the CO2 Flooding Injection–Production Environment

Comparison of 3%-Cr steel and carbon steel corrosion behavior as well tubing materials in CO2–H2S environment

Corrosion Behavior of Oil Tube Steels under Conditions of Multiphase Flow Saturated with Super-Critical Carbon Dioxide

The role of Cr content on the corrosion resistance of carbon steel and low-Cr steels in the CO2-saturated brine

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion Investigation of Commercially Available Linepipe Steel in CO2 Environment

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment

Research on the Corrosion Behavior of Q235 Pipeline Steel in an Atmospheric Environment through Experiment

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Corrosion Behavior of X65 Pipeline Steel: Comparison of Wet–dry Cycle and Full Immersion

CO2 corrosion behavior of simulated heat-affected zones for X80 pipeline steel

Experiment on the Anti-corrosion Property of Chrome Molybdenum Steel Tube in Naphthenic Acid Environment

Effect of Flow on the Corrosion Behavior of Pipeline Steel in Supercritical CO2 Environments with Impurities

Effect of Exposure Time on the Corrosion Rates of X70 Steel in Supercritical CO2/SO2/O2/H2O Environments

Corrosion Behavior of X65 Steel in Carbon Dioxide Solution under High Temperature and High Pressure

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Corrosion behavior study on heat treated API X70 pipeline steel exposed in different aggressive environments

Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2

Analysis Cracking Corrosion on Carbon Steel Pipes API 5L-X65 In Solution 7700 ml Aquades, 250 ml Acetic Acid and 50 ml Ammonia with Gas CO2 and H2S in Saturation Condition

Performance of two high-strength steels under electrochemical corrosive and stressed conditions