Abstract:The aim of this study was to reveal the macroscopic and mesoscopic deterioration behaviors of concrete under the coupling effect of chlorine salt erosion and the freezing–thawing cycle. The rapid freezing–thawing test was carried out in a 5% chlorine salt environment. The macroscopic characteristics of concrete were analyzed by testing the mass, the relative dynamic modulus of elasticity, and the compressive strength of concrete under different freezing–thawing cycles. Using CT scanning technology and three-dimensional reconstruction technology, the pore structure, CT value, and surface deviation of concrete before and after freezing–thawing were analyzed. Based on the changes of solid volume, pore volume, and solid CT value of concrete, the calculation method of relative CT value was proposed, and the damage model was established with relative CT value as the damage variable. The results demonstrate that the mass loss rate decreases in the beginning and then increases in the process of chlorine salt erosion and freezing–thawing, and the smaller the concrete size, the greater the mass loss rate. The relative dynamic modulus of elasticity decreases gradually, slowly at the initial stage and then at a faster rate, and the compressive strength loss rate increases gradually. The pore quantity, porosity, and volume loss rate of concrete increase in a fluctuating manner, whereas the relative CT value decreases. The comprehensive analysis shows that the chlorine salt frost resistance of concrete is negatively related to the water-cement ratio when the freezing–thawing cycle is fixed. The damage model could better reflect the freezing–thawing damage degree of concrete with different water cement ratios, and the damage evolution process is well described by the Weibull function.

Degradation mesomechanism of concrete deteriorated by soft water

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Mesomechanism of Tensile Strength Reduction and Tension Constitutive Model of Saturated Concrete

Micro-mechanism of Static and Dynamic Strengths for Saturated Concrete

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Meso-mechanism of Effects of Free Water on Mechanical Properties of Concrete under Confined Compression

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Degradation effect of seawater on the long-term dynamic behavior of artificially cemented sand

Investigating the Self-Healing Performance of Cracked Undersea Constructions

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

New concrete cracking model established based on fracture mechanics and damage theory

MESOMECHANICS ANALYSIS OF COMPRESSIVE STRENGTH AND CONSTITUTIVE EQUATION OF WET CONCRETE

Decay of fracture parameters of concrete under sulfate environments

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Impact of Fracture–Seepage–Stress Coupling on the Sustainability and Durability of Concrete: A Triaxial Seepage and Mechanical Strength Analysis

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

Experimental Study on the Damage and Deterioration Behaviour of Deep Soft Rock under Water-Rock Interaction

EXPERIMENTS ON SATURATED CONCRETE UNDER DIFFERENT SPLITTING TENSILE RATE AND MECHANISM ON STRENGTH CHANGE