Abstract:Ultra high toughness cementitious composite (abbreviated as UHTCC) shows significant pseudo strain hardening behavior and offers prominent tension strain ability of more than 3% when subjected to uniaxial tension load. The failure pattern of the UHTCC components exhibits multiple fine cracks with crack width lower than 100μm even corresponding to the ultimate tensile strain state. Four-point bending investigations of reinforced ultra high toughness cementitious composite (RUHTCC) members without web reinforcement have been carried out due to the excellent crack dispersion and strain energy absorption abilities of UHTCC material, aiming at design issues of strictly anti-cracking structures or aseismic design in key parts of structures such as beam column joint when using UHTCC. The moment-curvature curves have been measured and compared with the theoretical analysis proposed before. There is a reasonable agreement between them, especially that both moment and curvature present little difference before yielding. According to experimental results of RUHTCC beams with three different reinforcement ratios, UHTCC can delay yielding of reinforcements and improve load bearing capacity and ductility of structures or components compared with ordinary reinforced concrete beams, then steel products can be saved. The possibility of corrosion should be evidently reduced in respect that RUHTCC can effectively control crack. Accordingly, durability of structures improves by using UHTCC members.

Experimental Study on Fracture Performance of Ultra-High Toughness Cementitious Composites with J-integral

Experimental Study on Stress Wave Propagation in Ultra High Toughness Cementitious Composites

Experimental study on fracture evaluation criterion of ultra-high toughness cementitious composites

Study on Flexural Fatigue Life of Ultra-High Toughness Cementitious Composites under Constant Amplitude Cyclic Loading

Research on Flexural Properties and Flexural Toughness Evaluation Method of Ultra High Toughness Cementitious Composites

Experimental Study On Flexural Fatigue Property Of Ultra-High Toughness Cementitious Composites

Study Of Flexural Response In Strain Hardening Cementitious Composites Based On Proposed Parametric Model

Uniaxial Tensile Experiments of Ultra-High Toughness Cementitious Composite

Experimental measurement and analysis of the axial compressive stress-strain curve of Ultra High Toughness Cementitious Composites

STUDY ON FRACTURE PROCESS OF CONCRETE THREE-POINT BENDING BEAMS RETROFITTED WITH UHTCC

Experimental Study and Theoretical Models on Compressive Properties of Ultrahigh Toughness Cementitious Composites

STUDY ON CORRESPONDING RELATIONSHIPS BETWEEN FLEXURAL LOAD-DEFORMATION HARDENING CURVES AND TENSILE STRESS-STRAIN HARDENING CURVES OF UHTCC

Four Point Bending Experimental Investigation on Reinforced Ultra High Toughness Cementitious Composite Beams

Research on performance of new-type frame joints of ultra-high toughness cementitious composites

Shear Fracture Performance of the Interface Between Ultra-High Toughness Cementitious Composites and Reactive Powder Concrete

Toughness evaluation of ultra-high toughness cementitious composite specimens with different depths

Determination of energy consumption in the fracture plane of Ultra High Toughness Cementitious Composite with direct tension test

Analysis and experiment of reinforced ultra-high toughness cementitious composite flexural members

Investigation on crack propagation law of ultra-high toughness cementitious composites under fatigue flexure

Research on behavior of ultra-high toughness cementitious composites reinforced frame joints

Improvement of the flexural and cracking behavior of RC beams using ultra-high toughness cementitious composites(I):theoretical analysis