Investigation on Compressive Fatigue Damage Process of Ultra-High Toughness Cementitious Composites
Botao Huang,Qinghua Li,Shilang Xu,Baomin Zhou
DOI: https://doi.org/10.21012/fc9.116
2016-01-01
Abstract:Ultra-high toughness cementitious composites (UHTCC) is a kind of cementitious material reinforced by random distributed short fibers, which was proposed by Li and Leung and was designed with micromechanical principles to achieve the strain hardening behavior. This material has potential use in particular environments and structures that experience repeated or fatigue loads. Considering that the fatigue behavior of ultra-high toughness cementitious composites under compression is crucial for its application in certain conditions (e.g. airport runway and road pavements) and fatigue damage of structural components might be affected by both the flexural and compressive fatigue behaviors, the available work is rather limited and a better understanding of the compressive fatigue behavior is required. In this study, a series of monotonic and fatigue tests were performed to investigate the fatigue behavior of this material under compression. Compressive fatigue tests were conducted on 32 cylinder specimens (70 mm in diameter and 140 mm in height). The loading frequency of fatigue tests was set as 4 Hz and the maximum stress was 90%, 85%, 80%, 75%, 70% and 65% of the compressive strength with the stress ratio (the ratio between the minimum fatigue loads to the maximum fatigue load) set constant as 0.1. The S N relationship of ultra-high toughness cementitious composites was given, which indicates that the fatigue life of this material is higher than that of plain concrete and steel fiber reinforced concrete under the same stress level. It is observed that, the specimen failure mode of ultra-high toughness cementitious composites is similar to that of strain softening fiber reinforced concrete. The failure surface and damage process of this material were investigated. A new failure mode of PVA fiber with crush end was discovered with the help of SEM analysis and EDS analysis. This failure mode forms by the ruptured end of fibers experiencing repeated crushing and friction. Besides, based on the various failure modes of PVA fibers, the fatigue failure surface could be divided into three regions, including fatigue source region, transition region and crack extension region. During fatigue failure process, micro cracks initiate in the fatigue source region, propagate in the transition region and form main crack in the crack extension region.