Abstract:Superacid catalyst SO42--ZrO2/TiO2 was applied in esterification of Acetic Acid and Butanol. The particle size of ZrO2 in the catalyst was about 12.5 nm. In catalyst preparation conditions, the effect factor order on catalytic activity is H2SO4 concentration ＞ calcination temperature ＞ ZrO2 supported content. The optimum preparation condition is as follows: ZrO2 content 3.5g/g; calcination temperature 600℃, and H2SO4 concentration 0.5mol/L. The catalytic activity is 96.5 vol%.SO42-/MxOy solid superacid is a kind of green catalyst, whose application perspective is bright. In this paper, SO42--ZrO2/TiO2 solid superacid was prepared with nanometer compound carrying method. The acidic strength of catalysts was measured with the following Hammett indicators, 2,4-dinitrofluorobenzene (H0=-14.52) and p-nitrochlorobenzene (H0=-12.70). Catalytic activity was evaluated with esterification reaction of Acetic Acid and Butanol. Reaction temperature was at 105℃, and reaction time was only 1h. The conversion rate of Acetic Acid was analyzed by a gas chromatograph (GC-14C SHIMADZU in Japan)The experimental results showed that H2SO4 concentration had more influences on catalytic activity than other two factors, calcination temperature and ZrO2 supported content. Since sulfur absorbed on the surface of metal oxides is necessary to the acidity of SO42-/MxOy solid superacid,H2SO4 concentration in impregnation solution is needed enough high. But, it can't be too much high,otherwise, Zirconium sulfate formed on the catalyst surface will be harmful influences on catalytic activity. In researched cover, 0.5mol/L H2SO4 concentration is the most suitable, and the catalyst prepared with this concentration has very strong acidity.The optimum preparation condition is as follows: ZrO2 content 3.5g/g; calcination temperature 600℃, and H2SO4 concentration 0.5mol/L. In the catalyst prepared with above conditions, the acidic strength (H0) of the catalyst is smaller than ＜-14.52, and catalytic activity is 96.5 vol%. When it was re-used

Synthesis and characterization of S2O8^2-/ZrO2 SrFe12O19 strontium magnetic solid acid catalyst

Preparation of Fibrous SO42-/ZrO2-Nio Solid Acid Catalyst, Characterization and its Catalytic Properties

Preparation of Fibrous SO<sub>4</sub><sup>2-</sup>/ZrO<sub>2</sub>-Nio Solid Acid Catalyst, Characterization and Its Catalytic Properties

Preparation and Characterization of the Magnetic Nano-Size SO2-4/TiO2-Fe3O4 Catalysts

Metallic oxide-modified sulfated zirconia: an environment-friendly solid acid catalyst

High Catalytic Activity of Magnetic FeOx/NiOy/SBA-15: the Role of Ni in the Bimetallic Oxides at the Nanometer Level

Highly Stable, Active and Recyclable Solid Acid Catalyst Based on Polymer-Coated Magnetic Composite Particles

Synthesis of Butyl Lactate on Magnetic Solid Superacid Catalysts

Catalysis of SO42--ZrO2/TiO2 Nanometer Solid Superacid

Novel Magnetically-Recoverable Solid Acid Catalysts with a Hydrophobic Layer in Protecting the Active Sites from Water Poisoning

Esterification And Transesterification On Al2o3-Doped Sulfated Tin Oxide Solid Acid Catalysts

Influence of Surface Modification of Srfe12o19 Particles with Oleic Acid on Magnetic Microsphere Preparation

Preparation of Solid Acid SO2- 4/Fe2O3-SiO2 by Stearic Acid Method and Preliminary Study on Its Catalytic Activity

Esterification and Transesterification on Al 2 O 3 -Doped Sulfated Tin Oxide Solid Acid Catalysts

In-situ Reduction-Passivation Synthesis of Magnetic Octahedron Accumulated by Fe@Fe3O4-C Core@complex-Shell for the Activation of Persulfate

CoFe2O4 Nanocrystals Mediated Crystallization Strategy for Magnetic Functioned ZSM-5 Catalysts

Preparation of SiO2/(γ-Fe2O3-SiO2 ) Magnetic Catalyst Carrier

Magnetic Separation of Metal Sulfides/oxides by Fe 3 O 4 at Room Temperature and Atmospheric Pressure

Preparation and Catalytic Performance of SO2-4/ZrO2-SiO2 Solid Superacid

Synthesis of a novel magnetic CuFe2O4/zeolite composite catalyst and its catalytic oxidation performance

Sulfonic Acid-Functionalized Core-Shell Fe 3 O 4 @carbon Microspheres As Magnetically Recyclable Solid Acid Catalysts