Microstructure and corrosion resistance of Fe-based amorphous coating prepared by detonation spray
Shuai Cui,Haimin Zhai,Wensheng Li,Xiangjuan Fan,Xuqiang Li,Weichao Ning,Dangsheng Xiong
DOI: https://doi.org/10.1016/j.surfcoat.2020.126096
IF: 4.865
2020-10-01
Surface and Coatings Technology
Abstract:<p>The Fe-based amorphous coatings were successfully prepared on the surface of Q235 carbon steel by detonation spraying process under different oxygen-fuel ratio (2.5, 2.0 and 1.7), and the resultant coatings were named as coating A, B and C. The macro-structure and corrosion behaviors of the coating were investigated in detail by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) in 3.5 wt% NaCl solution. It was found that the corrosion resistance is correlated with the microstructure, phase component, and porosity of Fe-based amorphous coating. The morphology of the microdomains showed that coating B was highest dense and had no obvious defects, and the thickness, porosity was about 220 ± 10 μm, and 0.5% respectively. The electrochemical tests showed that Fe-based amorphous coating has effective protection for Q235 carbon steel in 3.5 wt% NaCl solution, and coating B has the highest corrosion potential (−283 mV vs −501 mV for coating A, −336 mV for coating C), and lowest corrosion current density (5.14 μA cm<sup>−2</sup> vs 17.54 μA cm<sup>−2</sup> for coating A, 9.71 μA cm<sup>−2</sup> for coating C), and the highest the |Z| value (10<sup>3.7</sup> vs 10<sup>3.1</sup> for coating A, 10<sup>3.4</sup> for coating C), which indicates that coating B has superior corrosion resistance. Besides, as the oxygen-fuel ratio changes from 2.5 to 1.7, the corrosion mechanism of the coating changes from inner corrosion to galvanic corrosion.</p>
physics, applied,materials science, coatings & films