Fatigue tests of point-supported tempered and laminated glass panels under cyclic loading

Shu Ganping,Lu Ruihua,Li Haiyun,Shi Yongjiu,Yuanqing Wang

DOI: https://doi.org/10.3969/j.issn.1001-0505.2012.04.025

2012-01-01

Abstract:In order to study the mechanical properties of four-point-supported glass panel under cyclic loading, fatigue tests were carried out on 8 tempered glass panels and 15 laminated glass panels under cyclic concentrated force. The deflections and the stresses at the key points during the loading process were measured. Experiments show that the load-center deflections of point-supported tempered glass panels slightly non-linearly rise with increasing cyclic loading, and the bending stiffness of tempered glass panels does not change with the increase of cyclic number. The load-center deflection curves of the laminates under dynamic load are related to ambient temperature. There is no hysteresis loop occurs at ambient temperature below 15°C, while pronounced hysteresis loop at occurs 22 to 30°C. The load-center deflections of laminated glass panels under a constant amplitude cyclic loading grow with the increase of cycles, but the increment of deflections are reduced gradually and after 5×10 4 cyclic loadings these is almost no more increment of deflection. Both tempered glass and laminated glass panels after the fatigue tests show no static flexural strength reduction after 5×10 5 cyclic loadings. The results indicate that point-supported tempered glass and laminated glass panels both have good fatigue capacity.