TiN refinement and resultant grain refinement in magnesium-treated ultra-pure ferritic stainless steel
Xingzhi Zhou,Deyong Wang,Jun Tian,Tianpeng Qu,Zhixiao Zhang,Yanping Wang,Xianglong Li,Dong Hou
DOI: https://doi.org/10.1016/j.matchar.2024.113659
IF: 4.537
2024-01-20
Materials Characterization
Abstract:The phenomena and mechanisms for TiN and corresponding as-cast grain refinement in magnesium-treated ultra-pure ferritic stainless steel (ultra-FSS) have been systematically investigated in this study, and two samples were prepared as the Initial and magnesium-treated samples. A new research method, X-ray diffraction coupled with electrochemical impedance spectroscopy, was conducted to reveal the relationship among the solute atoms, TiN, and solidification structure; after magnesium treatment, the solidification structure is refined resulting from the promoted precipitation of TiN and the corresponding decrease of solute Ti atoms. From the results of TiN inclusions coupled with mechanism analysis, it is concluded that the promoted precipitation and refinement of TiN can be attributed to (i) the pure oxides possessing low lattice misfits with TiN along at least one orientation relationship, (ii) multiphase complex oxides including at least one phase possessing extremely low lattice misfits with TiN, and (iii) sufficient oxides. Based on the results of macro−/microstructures and solidification processes, the general rule of solidification for metallic materials can be perfected as: the metal with more finer nucleating particles inoculated, higher latent heat of fusion/crystallization, smaller critical undercooling degree, wider nucleation-growth interval, and narrower solidification interval usually yields finer grains. Grain refinement of ultra-FSS through TiN is comprehensively evaluated by the interfacial wetting-lattice mismatch heterogeneous nucleation model; the higher value of the heterogeneous nucleation rate is, the higher equiaxed grain ratio and finer as-cast grain for the solidification structure are. Focused ion beam-transmission electron microscope was utilized to reveal the orientation relationships among magnesium-bearing oxide, TiN, TiC, and δ-Fe, directly confirming that the TiN refinement through oxides can be ascribed to the highly similar crystal structures.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing