Study on the mechanism of AF nucleation induced by complex oxide inclusions after LF refining in oxide metallurgical steel
Xiao Jia,Yinping Chen,Hengkun Li,Yulong Yang,Bin Wang,Bingxing Wang
DOI: https://doi.org/10.1016/j.matchar.2023.113239
IF: 4.537
2023-08-15
Materials Characterization
Abstract:The ladle furnace refining process (before LF, add Ti, add Al, add Mg, add Ca) of oxide metallurgical steel was sampled, and the effect of complex oxide inclusions generated after LF refining on acicular ferrite (AF) nucleation were studied by SEM, TEM, TKD and EBSD. The results show that the complex oxide inclusions after LF refining are composed of MgAl 2 O 4 , CaTiO 3 , TiO 2 , TiN, and MnS. Among them, MgAl 2 O 4 , CaTiO 3 , TiO 2 and TiN have NW orientation relationship with adjacent AF laths. There are Mn depletion zone(MDZ) with a width of about 200 nm outside MgAl 2 O 4 , CaTiO 3 , TiO 2 and MnS. Some AF laths can be nucleated by different inclusions under the combined action of MDZ mechanism and lattice mismatch mechanism. The first principle calculations show that MgAl 2 O 4 , CaTiO 3 and TiO 2 all have cation vacancies, and the diffusion of Mn ions into cation vacancies has thermodynamic advantages. The formation of MDZs is the combined effect of MnS precipitation on oxidized inclusions and Mn ions occupying cation vacancies in inclusions.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing